Mechanochemical synthesis of non-stoichiometric copper sulfide Cu1.8S applicable as a photocatalyst and antibacterial agent and synthesis scalability verification.

An effort to prepare different non-stoichiometric CuxSy compounds starting from elemental precursors using mechanochemistry was made in this study. However, out of the 7 stoichiometries tested, it was only possible to obtain three phases: covellite CuS, chalcocite Cu2S and digenite Cu1.8S and their mixtures. To obtain the digenite phase with the highest purity, the Cu : S stoichiometric ratio needed to be fixed at 1.6 : 1. The reaction between copper and sulfur was completed within a second range, however, milling was performed for up to 15 minutes until the equilibrium in phase composition between digenite and covellite was reached. The possibility of preparing the product in a 300 g batch by eccentric vibratory milling in 30 minutes was successfully verified at the end. The estimated crystallite sizes for the digenite Cu1.8S obtained via lab-scale and scalable experiments were around 12 and 17 nm, respectively. The obtained products were found to be efficient photocatalysts under visible light irradiation in the presence of hydrogen peroxide, being capable of the complete degradation of the Methyl Orange dye in a concentration of 10 mg L-1 in 2 hours. Finally, the antibacterial potential of both lab-scale and large-scale industrial products was proven and, regardless of the manufacturing scale, the nanoparticles retained their properties against bacterial cells.

Properties of CuFeS2/TiO2 Nanocomposite Prepared by Mechanochemical Synthesis.

CuFeS2/TiO2 nanocomposite has been prepared by a simple, low-cost mechanochemical route to assess its visible-light-driven photocatalytic efficiency in Methyl Orange azo dye decolorization. The structural and microstructural characterization was studied using X-ray diffraction and high-resolution transmission electron microscopy. The presence of both components in the composite and a partial anatase-to-rutile phase transformation was proven by X-ray diffraction. Both components exhibit crystallite size below 10 nm. The crystallite size of both phases in the range of 10-20 nm was found and confirmed by TEM. Surface and morphological properties were characterized by scanning electron microscopy and nitrogen adsorption measurement. Scanning electron microscopy has shown that the nanoparticles are agglomerated into larger grains. The specific surface area of the nanocomposite was determined to be 21.2 m2·g-1. Optical properties using UV-Vis and photoluminescence spectroscopy were also investigated. CuFeS2/TiO2 nanocomposite exhibits strong absorption with the determined optical band gap 2.75 eV. Electron paramagnetic resonance analysis has found two types of paramagnetic ions in the nanocomposite. Mössbauer spectra showed the existence of antiferromagnetic and paramagnetic spin structure in the nanocomposite. The CuFeS2/TiO2 nanocomposite showed the highest discoloration activity with a MO conversion of ~ 74% after 120 min irradiation. This study has shown the possibility to prepare nanocomposite material with enhanced photocatalytic activity of decoloration of MO in the visible range by an environmentally friendly manner.

Sustainable Synthesis of Cadmium Sulfide, with Applicability in Photocatalysis, Hydrogen Production, and as an Antibacterial Agent, Using Two Mechanochemical Protocols.

CdS nanoparticles were successfully synthesized using cadmium acetate and sodium sulfide as Cd and S precursors, respectively. The effect of using sodium thiosulfate as an additional sulfur precursor was also investigated (combined milling). The samples were characterized by XRD, Raman spectroscopy, XPS, UV-Vis spectroscopy, PL spectroscopy, DLS, and TEM. Photocatalytic activities of both CdS samples were compared. The photocatalytic activity of CdS, which is produced by combined milling, was superior to that of CdS, and was obtained by an acetate route in the degradation of Orange II under visible light irradiation. Better results for CdS prepared using a combined approach were also evidenced in photocatalytic experiments on hydrogen generation. The antibacterial potential of mechanochemically prepared CdS nanocrystals was also tested on reference strains of E. coli and S. aureus. Susceptibility tests included a 24-h toxicity test, a disk diffusion assay, and respiration monitoring. Bacterial growth was not completely inhibited by the presence of neither nanomaterial in the growth environment. However, the experiments have confirmed that the nanoparticles have some capability to inhibit bacterial growth during the logarithmic growth phase, with a more substantial effect coming from CdS nanoparticles prepared in the absence of sodium thiosulfate. The present research demonstrated the solvent-free, facile, and sustainable character of mechanochemical synthesis to produce semiconductor nanocrystals with multidisciplinary application.

Heterostructured g-CN/TiO2 Photocatalysts Prepared by Thermolysis of g-CN/MIL-125(Ti) Composites for Efficient Pollutant Degradation and Hydrogen Production.

Photocatalysts composed of graphitic carbon nitride (g-CN) and TiO2 were efficiently prepared by thermolysis of the MIL-125(Ti) metal organic framework deposited on g-CN. The heterojunction between the 12 nm-sized TiO2 nanoparticles and g-CN was well established and the highest photocatalytic activity was observed for the g-CN/TiO2 (3:1) material. The g-CN/TiO2 (3:1) composite exhibits high visible light performances both for the degradation of pollutants like the Orange II dye or tetracycline but also for the production of hydrogen (hydrogen evolution rate (HER) up to 1330 µmolh-1g-1 and apparent quantum yield of 0.22% using NiS as a cocatalyst). The improved visible light performances originate from the high specific surface area of the photocatalyst (86 m2g-1) and from the efficient charge carriers separation as demonstrated by photoluminescence, photocurrent measurements, and electrochemical impedance spectroscopy. The synthetic process developed in this work is based on the thermal decomposition of metal organic framework deposited on a graphitic material and holds huge promise for the preparation of porous heterostructured photocatalysts.

Synthesis of Core/Shell ZnO/rGO Nanoparticles by Calcination of ZIF-8/rGO Composites and Their Photocatalytic Activity.

A facile two-step method was developed to prepare core/shell ZnO/rGO particles from ZIF-8/rGO composites. ZIF-8 particles were first grown at the surface of rGO sheets. Next, ZIF-8 particles were transformed into ZnO particles by thermal decomposition under air at 500 °C. All materials were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Raman spectroscopy, thermogravimetric analysis, and Brunauer-Emmett-Teller analyses. Results obtained show that ZIF-8 particles strongly associate with rGO sheets and that the calcination of this material produces porous core/shell ZnO/rGO particles with an average diameter of ca. 40 nm. The wt % of rGO associated with ZIF-8 particles was varied from 5 to 20%. The ZnO/rGO (10%) particles exhibit the highest photocatalytic activity for the degradation of the Orange II dye under simulated solar light irradiation of weak intensity (5 mW/cm2). This high photocatalytic activity was demonstrated to originate from superoxide O2 •- radicals due to the efficient trapping of photogenerated electrons in ZnO by rGO.