Characterizing the Interface Scaling of High χ Block Copolymers near the Order-Disorder Transition.

Advancements in the directed self-assembly of block copolymers (BCPs) have prompted the development of new materials with larger effective interaction parameters (χe). This enables BCP systems with phase separation at increasingly small degrees of polymerization (N). Very often these systems reside near the order-disorder transition and fit between the weak and strong segregation limits where the behavior of BCP systems is not as thoroughly understood. Utilizing resonant soft X-ray reflectivity (RSoXR) enables both the BCP pitch (L0) and interface width (wM) to be determined simultaneously, through a direct characterization of the composition profile of BCP lamellae oriented parallel to a substrate. A series of high χe BCPs with χe ranging from ≈0.04 to 0.25 and χeN from 19 to 70 have been investigated. The L0/wm ratio serves as an important metric for the feasibility of a material for nanopatterning applications; the results of the RSoXR measurement are used to establish a relationship between χe and L0/wm. The results of this analysis are correlated with experimentally established limits for the functionality of BCPs in nanopatterning applications. These results also provide guidance for the magnitude of χe needed to achieve small interface width for samples with sub-10 nm L0.

Quantifying the Interface Energy of Block Copolymer Top Coats.

Block copolymers (BCPs) have the potential to play a key role in templating materials for nanoscale synthesis. BCP lithography likely will be one of the first examples of BCP-based nanomanufacturing implemented in a production setting. One of the challenges in implementing BCP lithography is that the lamella need to be oriented perpendicular to the substrate. For many systems, this requires control over interfacial energies for both components at the substrate and interface. Top coats can be designed to provide a neutral interface for both blocks on the BCP surface. The preferentiality of the top coat as a function of composition has been determined qualitatively by examining the orientation of a BCP after annealing with a top coat. Measurements of the interfacial width between the top coat and homopolymers allows the interface energy to be quantitatively determined. Resonant soft X-ray reflectivity measurements on top coat/homopolymer pairs were used to extract the Flory-Huggins parameter (χ) and interface energy (γ) as a function of top coat composition. The difference between χ and γ for each top coat/homopolymer pair was minimized at compositions that resulted in the top coat promoting perpendicular orientation. As the composition moved away from the neutral point the difference between χ and γ for each pair grew larger.