Pulsed laser deposited CoFe2O4 thin films as supercapacitor electrodes.

The influence of the substrate temperature on pulsed laser deposited (PLD) CoFe2O4 thin films for supercapacitor electrodes was thoroughly investigated. X-ray diffractometry and Raman spectroscopic analyses confirmed the formation of CoFe2O4 phase for films deposited at a substrate temperature of 450 °C. Topography and surface smoothness was measured using atomic force microscopy. We observed that the films deposited at room temperature showed improved electrochemical performance and supercapacitive properties compared to those of films deposited at 450 °C. Specific capacitances of about 777.4 F g-1 and 258.5 F g-1 were obtained for electrodes deposited at RT and 450 °C, respectively, at 0.5 mA cm-2 current density. The CoFe2O4 films deposited at room temperature exhibited an excellent power density (3277 W kg-1) and energy density (17 W h kg-1). Using electrochemical impedance spectroscopy, the series resistance and charge transfer resistance were found to be 1.1 Ω and 1.5 Ω, respectively. The cyclic stability was increased up to 125% after 1500 cycles due to the increasing electroactive surface of CoFe2O4 along with the fast electron and ion transport at the surface.

Mimicking the Synaptic Weights and Human Forgetting Curve Using Hydrothermally Grown Nanostructured CuO Memristor Device.

In the present investigation, we have fabricated copper oxide (CuO) thin film memristor by employing a hydrothermal method for neuromorphic application. The X-ray diffraction pattern confirms the films are polycrystalline in nature with the monoclinic crystal structure. The developed devices show analog memory and synaptic property similar to biological neuron. The size dependent synaptic behavior is investigated for as-prepared and annealed CuO memristor. The results suggested that the magnitude of synaptic weights and resistive switching voltages are dependent on the thickness of the active layer. Synaptic weights are improved in the case of the as-prepared device whereas they are inferior for annealed CuO memristor. The rectifying property similar to a biological neuron is observed only for the as-prepared device, which suggested that as-prepared devices have better computational and learning capabilities than annealed CuO memristor. Moreover, the retention loss of the CuO memristor is in good agreement with the forgetting curve of human memory. The results suggested that hydrothermally grown CuO thin film memristor is a potential candidate for the neuromorphic device development.

Safety and efficacy of hydroxyurea in children and adolescents with sickle/beta-thalassemia: two-year experience.

BACKGROUND: Hydroxyurea is a cytotoxic and myelosuppressive drug that has been used during recent years in the treatment of children with severe sickle cell disease. Nevertheless, questions remain regarding its role in young patients with no severe course, like sickle/beta-thalassemia (S/b-thal) patients often present. The aim of the present study was to evaluate the safety and efficacy of hydroxyurea in young patients with S/b-thal, which is the commonest form of the disease in Greece. PATIENTS-METHODS: Hydroxyurea was given in thirteen children with S/b-thal for 24 months and for that period clinical and laboratory evaluation of the children was performed. RESULTS: A reduction in pain crises and rate of hospitalization was noted. None of the patients presented with a severe clinical event, related to the disease during the study period. A significant increase in hemoglobin, hemoglobin F, mean corpuscular volume, and mean corpuscular hemoglobin and a decrease in reticulocyte count, white blood cell and platelet count, and total bilirubin level was noted. With regards to adverse events, these were transient, short-term and dose-dependable. CONCLUSIONS: To the best of our knowledge, this is the first study to specifically assess the effect of hydroxyurea therapy in young patients with S/b-thal and the results indicate is safe and efficacious in this patient cohort. Hippokratia 2015; 19 (2):172-175.

Autotrophic nitrogen removal by a two-step SBR process applied to mixed agro-digestate.

The aim of this research was to evaluate the applicability of partial-nitritation/anammox processes for biological N removal from a centrifuge supernatant coming from a full scale anaerobic digester fed on a mixture of piggery manure, poultry manure, and agro-wastes. Stable partial nitritation was achieved at pilot-scale (650L SBR), obtaining a suitable influent for the anammox lab-scale SBR reactor (3L). The anammox lab scale reactor was fed with increasing fractions of the partial nitritation effluent, blended with synthetic wastewater. In the last 100days no dilution was used. The nitrogen loading rate applied to the anammox reactor was 0.5-0.6gNL(-)(1)d(-)(1) and the average nitrogen removal was 91±10%. During the first days of operation with undiluted supernatant, the maximum anammox activity in the SBR decreased, but recovered afterwards, suggesting the ability of the anammox biomass to acclimate to the wastewater. N2O emissions in both reactors were also measured.

Laboratory investigation of platelet function in patients with thalassaemia.

The aim of this study was to investigate platelet function in patients with thalassaemia and to detect any relation to chelation treatment (deferasirox or deferiprone/deferiprone plus desferioxamine). Thirty-three transfusion-dependent patients with thalassaemia were included. The investigation consisted of aggregation testing of platelet-rich plasma by light transmission aggregometry (LTA) with the use of 5 agonists as well as the global test of haemostasis by means of the PFA-100 platelet function analyser. In 66.67% of the patients, there was reduced LTA to at least one agonist and in 18.18% there was reduced LTA to two or more agonists. The PFA-100 test was prolonged in 60.6% of the cases. An abnormal LTA and a prolonged PFA-100 time were recorded in 33.3% of the patients and 27.4% had a normal aggregation and PFA-100 test. No correlation between chelation regimen and either LTA or PFA-100 test was found. The abnormal LTA can be explained either by the release of ADP from the haemolysed red blood cells, which leads to defective platelet aggregation, or by the presence of two platelet populations. An in vitro effect without an in vivo impact could be an alternative explanation. In patients with thalassaemia, the reduced LTA and the prolonged PFA-100 closure time could be an in vitro effect and has a close correlation to the bleeding phenotype of each patient.

MBR fouling control and permeate quality enhancement by polyaluminium chloride dosage: a case study.

Scope of this study was to evaluate the effectiveness of a metal salt (polyaluminium chloride, PACl) dosage into a pilot-scale MBR (membrane bioreactor) in terms of fouling control and permeate quality enhancement, especially with reference to specific textile macro-pollutants (dyes and surfactants). The pilot plant was fed with a mixed domestic-textile wastewater (textile wastewater accounted for 65% of total flow and for 70% of total chemical oxygen demand, COD, load) and operated for 7.5 months without flux enhancers (step 1) and 3 months with the addition of PACl (step 2). The optimum dose was defined performing a jar-test campaign between step 1 and step 2 (12.5 mg gMLSS(-1) that corresponds to 0.4 g d(-1)). The addition of PACl resulted in a significant decrease of the filtration resistance due to cake layer formation (R(c), -65.4%) and of the irreversible fouling rate, evaluated as the average variation per unit time of the filtration resistance due to foulants adsorption on membrane pore wall (FR, -45.3%). As for permeate quality, removal rates related to total phosphorus and textile macro-parameters such as colour and anionic surfactants, increased by +64, +16 and +7%, respectively. No significant effect was observed on COD, non-ionic surfactants and nitrogen compounds removal.

Influence of thermal extraction of extracellular polymeric substances on cell integrity in activated sludge and membrane bioreactor samples.

The influence of the soluble microbial products (SMP) and extracellular polymeric substances (EPS) heating extraction method on cell viability was evaluated for each phase of the protocol using epifluorescence microscopy. In addition, the effect of different centrifugation conditions (2700 g at 24 degrees C; 12,000 g at 4 degrees C) was also tested. Sludge samples were collected from a conventional wastewater treatment and a membrane bioreactor (MBR) pilot plant fed in parallel. Results show that different centrifugation parameters do not induce cell membrane damaging. Heating significantly influences membrane integrity; for instance, 75 to 90% of initial viable cells are damaged during this phase, possibly leading to the predominance of protein compared to carbohydrate content. The protein content in EPS is 60 to 88 mg bovine serum albumin/ g volatile suspended solids (VSS); higher values observed in MBR sludge samples are probably attributable to the different characteristics of microbial flocs and process operating parameters. Carbohydrate concentrations are not significantly different regardless of applied procedure and sludge type, and are between 10.4 to 11.6 mg glucose/g VSS.