Aluminum matrix composites (AMCs) reinforced by aluminum nitride were prepared by mechanical alloying followed by a simple press and sintering method. Milling began under vacuum and after a period of between 1 and 4 h, NH3 gas flow (1 cm³/s) was incorporated until the total milling time of 5 h was reached. Results show that in addition to the strain hardening taking place during mechanical alloying, NH3 plays an additional role in powder hardening. Thereby, the properties of the sintered compacts are strongly influenced by the amount of N incorporated into the powders during milling and the subsequent formation of AlN during the consolidation process. The obtained AMC reaches tensile strengths as high as 459 MPa and hardness much higher than that of the as-received aluminum compact.
RESUMO
The reaction [Ru(NH3)5pz]2+ + Co(C2O4)33- has been studied in aqueous solutions of p-sulfonatocalix[n]arene (n = 4, 6, and 8). The results are interpreted by using the pseudophase model. Results show that the rigidity and/or flexibility of the assembled rings have a great effect on the thermodynamics of inclusion of the guest into the host and, therefore, on the kinetics of the electron transfer processes that take place in these media. The obtained results are discussed from the viewpoint of two types of interactions: electrostatic and nonelectrostatic. From surface potential measurements, the guest-host interactions have been demonstrated to be mainly due to nonelectrostatic interactions, although the species are charged. So, the nonelectrostatic contribution to the equilibrium constant in all the calixarenes studied is 1 order of magnitude higher than the electrostatic one (Knel = 144 and 884 mol-1 dm3 for p-sulfonatocalix[n]arene (n = 4 and 6, respectively) and Kel approximately 10 mol-1 dm3). Electrostatic interactions also affect the kinetic results.