Sustainable Carbon Derived from Sulfur-Free Lignins for Functional Electrical and Electrochemical Devices.

Technical lignins, kraft, soda, lignoboost, and hydrolysis lignins were used for the production of carbon particles at different carbonization temperatures, 1000 °C and 1400 °C. The results showed that the lignin source and carbonization temperature significantly influenced the carbon quality and microstructure of the carbon particles. Soda lignin carbonized up to 1400 °C showed higher degree of graphitization and exhibited the highest electrical conductivity of 335 S·m-1, which makes it suitable for applications, such as electromagnetic interference shielding and conductive composite based structural energy storage devices. The obtained carbon particles also showed high surface area and hierarchical pore structure. Kraft lignin carbonized up to 1400 °C gives the highest BET surface area of 646 m2 g-1, which makes it a good candidate for electrode materials in energy storage applications. The energy storage application has been validated in a three-electrode set up device, and a specific capacitance of 97.2 F g-1 was obtained at a current density of 0.1 A g-1 while an energy density of 1.1 Wh kg-1 was observed at a power density of 50 W kg-1. These unique characteristics demonstrated the potential of kraft lignin-based carbon particles for electrochemical energy storage applications.

Hetero-Porous, High-Surface Area Green Carbon Aerogels for the Next-Generation Energy Storage Applications.

Various carbon materials have been developed for energy storage applications to address the increasing energy demand in the world. However, the environmentally friendly, renewable, and nontoxic bio-based carbon resources have not been extensively investigated towards high-performance energy storage materials. Here, we report an anisotropic, hetero-porous, high-surface area carbon aerogel prepared from renewable resources achieving an excellent electrical double-layer capacitance. Two different green, abundant, and carbon-rich lignins which can be extracted from various biomasses, have been selected as raw materials, i.e., kraft and soda lignins, resulting in clearly distinct physical, structural as well as electrochemical characteristics of the carbon aerogels after carbonization. The obtained green carbon aerogel based on kraft lignin not only demonstrates a competitive specific capacitance as high as 163 F g-1 and energy density of 5.67 Wh kg-1 at a power density of 50 W kg-1 when assembled as a two-electrode symmetric supercapacitor, but also shows outstanding compressive mechanical properties. This reveals the great potential of the carbon aerogels developed in this study for the next-generation energy storage applications requiring green and renewable resources, lightweight, robust storage ability, and reliable mechanical integrity.