The utilization of polarized neutrons is of great importance in scientific disciplines spanning materials science, physics, biology, and chemistry. However, state-of-the-art multilayer polarizing neutron optics have limitations, particularly low specular reflectivity and polarization at higher scattering vectors/angles, and the requirement of high external magnetic fields to saturate the polarizer magnetization. Here, we show that, by incorporating 11B4C into Fe/Si multilayers, amorphization and smooth interfaces can be achieved, yielding higher neutron reflectivity, less diffuse scattering, and higher polarization. Magnetic coercivity is eliminated, and magnetic saturation can be reached at low external fields (>2 militesla). This approach offers prospects for substantial improvement in polarizing neutron optics with nonintrusive positioning of the polarizer, enhanced flux, increased data accuracy, and further polarizing/analyzing methods at neutron scattering facilities.
RESUMO
Liquid aluminum containing the important alloying element magnesium in varying concentrations was analyzed using in-situ laser-induced breakdown spectroscopy (LIBS). Magnesium emission shows an exponential dependence on melt temperature that correlates well with the expected partial pressure of magnesium above the aluminum melt. Furthermore, comparison with LIBS measurements on corresponding solid samples supports the conclusion that a significant part of Mg emission from liquid metal samples originates from the vapor phase above the metal surface. Simultaneously, curves of growth measured over four orders of magnitude in Mg concentration reveal a level of self-absorption for liquid aluminum samples that is stronger than for solid aluminum samples having a corresponding Mg concentration, and beyond what is expected from conventional plasma models. The implications for measurements of volatile species in liquid metals in general are discussed.