RESUMO
Modification of electronic and chemical properties of a material by the introduction of another element into its lattice is one of the most common methods for designing new catalysts for different applications. In this work the effect of modifying molybdenum carbide with transition metals (Fe, Co, Ni, Cu), TM-Mo2C composites, upon the catalytic activity toward hydrogen evolution reaction (HER) in mild acidic and alkaline media has been studied. Catalysts were prepared by carbothermal reduction of molybdenum and TM oxides precursors and were characterized by different physicochemical techniques. Results evidenced a strong pH effect on the catalytic performance of TM-Mo2C, while, at pH = 5, inclusion of TM into the Mo2C lattice has a deleterious effect on the HER activity and, at pH = 9, a promoting effect was observed, highlighting the importance of considering specific operation conditions during the catalyst design process. Analysis of in situ near-edge X-ray adsorption data reveals a decrease on the oxidation state and average bond ionicity of dopant metal upon a pH increase, shedding light of the different effects of TMs on the resulting HER activity in acidic and alkaline media. Finally, stability tests demonstrated no deterioration on catalysts' performance after 8 h of continuous cycling within the HER working range, confirming the suitability of Mo2C materials as promising HER catalysts.
RESUMO
This study describes a systematic investigation of the electrocatalytic activity of poly[Ni(salen)] films, as catalysts for the electro-oxidation of Cn alcohols (Cn = methanol, ethanol, and glycerol) in alkaline medium. The [Ni(salen)] complex was electropolymerized on a glassy carbon surface and electrochemically activated in NaOH solution by cyclic voltammetry. X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy results indicate that during the activation step the polymeric film hydrolyzes, leading to the formation of ß-Ni(OH)2 spherical nanoparticles, with an average size of 2.4 ± 0.5 nm, encapsulated with the poly[Ni(salen)] film. Electrochemical results obtained together with the in situ Fourier transform infrared spectroscopy confirm that the electro-oxidation of methanol, ethanol, and glycerol occurs by involving a cycling oxidation of ß-Ni(OH)2 with the formation of ß-NiOOH species, followed by the charge transfer to the alcohols, which regenerates ß-Ni(OH)2. Analyses of the oxidation products at low potentials indicate that the major product obtained during the oxidation of methanol and glycerol is the formate, while the oxidation of ethanol leads to the formation of acetate. On the other hand, at high potentials (E = 0.6 V), there is evidence that the oxidation of Cn alcohols leads to carbonate ions as an important product.
RESUMO
Studies aiming at improving the activity and stability of dispersed W and Mo containing Pt catalysts for the CO tolerance in proton exchange membrane fuel cell (PEMFC) anodes are revised for the following catalyst systems: (1) a carbon supported PtMo electrocatalyst submitted to heat treatments; (2) Pt and PtMo nanoparticles deposited on carbon-supported molybdenum carbides (Mo2C/C); (3) ternary and quaternary materials formed by PtMoFe/C, PtMoRu/C and PtMoRuFe/C and; (4) Pt nanoparticles supported on tungsten carbide/carbon catalysts and its parallel evaluation with carbon supported PtW catalyst. The heat-treated (600 oC) Pt-Mo/C catalyst showed higher hydrogen oxidation activity in the absence and in the presence of CO and better stability, compared to all other Mo-containing catalysts. PtMoRuFe, PtMoFe, PtMoRu supported on carbon and Pt supported on Mo2C/C exhibited similar CO tolerances but better stability, as compared to as-prepared PtMo supported on carbon. Among the tungsten-based catalysts, tungsten carbide supported Pt catalyst showed reasonable performance and reliable stability in comparison to simple carbon supported PtW catalyst, though an uneven level of catalytic activity towards H2 oxidation in presence of CO is observed for the former as compared to Mo containing catalyst. However, a small dissolution of Mo, Ru, Fe and W from the anodes and their migration toward cathodes during the cell operation is observed. These results indicate that the fuel cell performance and stability has been improved but not yet totally resolved.
RESUMO
ABSTRACT Studies aiming at improving the activity and stability of dispersed W and Mo containing Pt catalysts for the CO tolerance in proton exchange membrane fuel cell (PEMFC) anodes are revised for the following catalyst systems: (1) a carbon supported PtMo electrocatalyst submitted to heat treatments; (2) Pt and PtMo nanoparticles deposited on carbon-supported molybdenum carbides (Mo2C/C); (3) ternary and quaternary materials formed by PtMoFe/C, PtMoRu/C and PtMoRuFe/C and; (4) Pt nanoparticles supported on tungsten carbide/carbon catalysts and its parallel evaluation with carbon supported PtW catalyst. The heat-treated (600 oC) Pt-Mo/C catalyst showed higher hydrogen oxidation activity in the absence and in the presence of CO and better stability, compared to all other Mo-containing catalysts. PtMoRuFe, PtMoFe, PtMoRu supported on carbon and Pt supported on Mo2C/C exhibited similar CO tolerances but better stability, as compared to as-prepared PtMo supported on carbon. Among the tungsten-based catalysts, tungsten carbide supported Pt catalyst showed reasonable performance and reliable stability in comparison to simple carbon supported PtW catalyst, though an uneven level of catalytic activity towards H2 oxidation in presence of CO is observed for the former as compared to Mo containing catalyst. However, a small dissolution of Mo, Ru, Fe and W from the anodes and their migration toward cathodes during the cell operation is observed. These results indicate that the fuel cell performance and stability has been improved but not yet totally resolved.