Dielectric surface-controlled low-voltage organic transistors via n-alkyl phosphonic acid self-assembled monolayers on high-k metal oxide.

In this paper, we report on n-alkyl phosphonic acid (PA) self-assembled monolayer (SAM)/hafnium oxide (HfO(2)) hybrid dielectrics utilizing the advantages of SAMs for control over the dielectric/semiconductor interface with those of high-k metal oxides for low-voltage organic thin film transistors (OTFTs). By systematically varying the number of carbon atoms of the n-alkyl PA SAM from six to eighteen on HfO(2) with stable and low leakage current density, we observe how the structural nature of the SAM affects the thin-film crystal structure and morphology, and subsequent device performance of low-voltage pentacene based OTFTs. We find that two primary structural factors of the SAM play a critical role in optimizing the device electrical characteristics, namely, the order/disorder of the SAM and its physical thickness. High saturation-field-effect mobilities result at a balance between disordered SAMs to promote large pentacene grains and thick SAMs to aid in physically buffering the charge carriers in pentacene from the adverse effects of the underlying high-k oxide. Employing the appropriate n-alkyl PA SAM/HfO(2) hybrid dielectrics, pentacene-based OTFTs operate under -2.0 V with low hysteresis, on-off current ratios above 1 x 10(6), threshold voltages below -0.6 V, subthreshold slopes as low as 100 mV dec(-1), and field-effect mobilities as high as 1.8 cm(2) V(-1) s(-1).

Study on the formation of self-assembled monolayers on sol-gel processed hafnium oxide as dielectric layers.

High dielectric constant (k) metal oxides such as hafnium oxide (HfO2) have gained significant interest due to their applications in microelectronics. In order to study and control the surface properties of hafnium oxide, self-assembled monolayers (SAMs) of four different long aliphatic molecules with binding groups of phosphonic acid, carboxylic acid, and catechol were formed and characterized. Surface modification was performed to improve the interface between metal oxide and top deposited materials as well as to create suitable dielectric properties, that is, leakage current and capacitance densities, which are important in organic thin film transistors. Attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy, contact angle goniometry, atomic force microscopy (AFM), and simple metal-HfO2-SAM-metal devices were used to characterize the surfaces before and after SAM modification on sol-gel processed hafnium oxide. The alkylphosphonic acid provided the best monolayer formation on sol-gel processed hafnium oxide to generate a well-packed, ultrathin dielectric exhibiting a low leakage current density of 2x10(-8) A/cm2 at an applied voltage of -2.0 V and high capacitance density of 0.55 microF/cm2 at 10 kHz. Dialkylcatechol showed similar characteristics and the potential for using the catechol SAMs to modify HfO2 surfaces. In addition, the integration of this alkylphosphonic acid SAM/hafnium oxide hybrid dielectric into pentacene-based thin film transistors yields low-voltage operation within 1.5 V and improved performance over bare hafnium oxide.