Effect of Different Surface Treatments on Porcelain-Resin Bond Strength.

PURPOSE: The aim of this study was to evaluate the effects of various surface treatments on the surface structure and shear bond strength (SBS) of different ceramics. MATERIALS AND METHODS: A total of 192 disk-shaped cores were prepared using two all-ceramic systems, of which 168 were submitted to SBS tests, and 24 were investigated by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The ceramics used were IPS Empress e.max (EX) lithium glass-ceramic and Vita In-Ceram Zirconia glass-infiltrated zirconia (ICZ). The specimens were randomly divided into seven groups (n = 12) on the basis of the surface treatment used: control; SB-sandblasting with 50 µm Al2 O3 particles; CJ-chairside silica coating with 30 µm SiO2 particles and silanization (Clearfil Porcelain Bond Activator); HF-etching in 5% hydrofluoric acid and silanization; ER-etching with an Er:YAG laser (10 W); ND-Nd:YAG laser etching (0.8 W); and FS-etching with a femtosecond laser (860 mW). A luting cement (Clearfil Esthetic) was photopolymerized on each treated ceramic disk. After subjecting the specimens to thermocycling (1000 cycles, 5°C to 55°C), SBS tests were performed using a universal testing machine. The data were analyzed with two-way ANOVA and Tukey's tests using a significance limit of 5%. RESULTS: Among the EX ceramics, the CJ (29.10 MPa) and HF (26.07 MPa) specimens had statistically higher SBS values. For the ICZ ceramics, the highest value (28.08 MPa) was obtained for the CJ specimens. CONCLUSIONS: Silanization after coating with silica improves the bond strengths of both EX and ICZ specimens, while HF etching is favorable only for the EX specimens.

Effect of various lasers on the bond strength of two zirconia ceramics.

OBJECTIVE: The purpose of this study was to compare and evaluate the effects of various laser systems on surface roughness and shear bond strengths of zirconia ceramics. MATERIAL AND METHODS: Seventy-two ceramic discs (10 mm×2 mm) obtained from two sintered zirconia ceramics (Zirkonzahn, Zirkonzahn Prettau(®)) were divided into two groups (n=36) according to the computer-aided design (CAD)-computer-aided manufacturing (CAM) technique and then further divided into three groups (n=12). Each group was treated with one of the following: (1) femtosecond (FS), (2) Nd:YAG (NY), and (3) Er:YAG (EY) lasers. After laser irradiation, a scanning electron micrograph (SEM) was taken at 500× magnification for qualitative examination. Following surface roughness measurement by profilometry, resin cement (Rely X U200) was bonded to the ceramic specimens using Teflon tubes (3 mm height, 4 mm diameter). Specimens were stored in distilled water at 37°C for 24 h and then thermal cycled for 5000 cycles. A shear bond strength (MPa) test was performed using a universal testing machine at a crosshead speed of 1 mm/min. Data were analyzed by two way analysis of variance (ANOVA) and Tukey honest significant difference (HSD) tests for pairwise comparisons among groups (p=0.05). RESULTS: MPa and roughness were significantly affected by laser type (p<0.001), and there was no significant interaction between the two zircon ceramics. The group irradiated with FS laser had significantly higher (p<0.05) roughness and MPa mean values than those of the other groups. No significant difference was found between the groups irradiated with NY and EY laser (p>0.05). In the SEM, the surfaces of the FS group were rougher than those of the NY and EY groups. NY and EY surfaces were nearly smooth. CONCLUSIONS: FS laser is an effective surface treatment for roughening surfaces of zirconia ceramics. Furthermore, it reveals the highest MPa.