RESUMO
The synthesis, physicochemical, and functional properties of composite solids resulting from the surface spread of oxidized indium species onto nanoplatelets of anatase were investigated. Both the size and the interaction between the indium- and titanium-containing components control the functional properties. In the reduction of CO2 to CO, the best samples have an indium content between ca. 2 and 5 mol % and showed an excess rate over the photo and thermo-alone processes above 33% and an energy efficiency of 1.3%. Subnanometric (monomeric and dimeric) indium species present relatively weak thermal catalytic response but strong thermo-photo promotion of the activity. A gradual change in functional properties was observed with the growth of the indium content of the solids, leading to a progressive increase of thermal activity but lower thermo-photo promotion. The study provides a well-defined structure-activity relationship rationalizing the dual thermo-photo properties of the catalysts and establishes a guide for the development of highly active and stable composite solids for the elimination and valorization of CO2.
RESUMO
Proton exchange membrane water electrolysis (PEMWE) is the technology of choice for the large-scale production of green hydrogen from renewable energy. Current PEMWEs utilize large amounts of critical raw materials such as iridium and platinum in the anode and cathode electrodes, respectively. In addition to its high cost, the use of Ir-based catalysts may represent a critical bottleneck for the large-scale production of PEM electrolyzers since iridium is a very expensive, scarce, and ill-distributed element. Replacing iridium from PEM anodes is a challenging matter since Ir-oxides are the only materials with sufficient stability under the highly oxidant environment of the anode reaction. One of the current strategies aiming to reduce Ir content is the design of advanced Ir-mixed oxides, in which the introduction of cations in different crystallographic sites can help to engineer the Ir active sites with certain characteristics, that is, environment, coordination, distances, oxidation state, etc. This strategy comes with its own problems, since most mixed oxides lack stability during the OER in acidic electrolyte, suffering severe structural reconstruction, which may lead to surfaces with catalytic activity and durability different from that of the original mixed oxide. Only after understanding such a reconstruction process would it be possible to design durable and stable Ir-based catalysts for the OER. In this Perspective, we highlight the most successful strategies to design Ir mixed oxides for the OER in acidic electrolyte and discuss the most promising lines of evolution in the field.
RESUMO
Proton exchange membrane water electrolysis is a promising technology to produce green hydrogen from renewables, as it can efficiently achieve high current densities. Lowering iridium amount in oxygen evolution reaction electrocatalysts is critical for achieving cost-effective production of green hydrogen. In this work, we develop catalysts from Ir double perovskites. Sr2CaIrO6 achieves 10 mA cm-2 at only 1.48 V. The surface of the perovskite reconstructs when immersed in an acidic electrolyte and during the first catalytic cycles, resulting in a stable surface conformed by short-range order edge-sharing IrO6 octahedra arranged in an open structure responsible for the high performance. A proton exchange membrane water electrolysis cell is developed with Sr2CaIrO6 as anode and low Ir loading (0.4 mgIr cm-2). The cell achieves 2.40 V at 6 A cm-2 (overload) and no loss in performance at a constant 2 A cm-2 (nominal load). Thus, reducing Ir use without compromising efficiency and lifetime.
RESUMO
The objective of this work is double-firstly to explore the photocatalytic efficiency of five different commercial TiO2 catalysts in the photodegradation of a mixture of pesticides classified by the EU as priority pollutants and secondly to analyze the correlation between their physicochemical properties and the inhibition of the studied photocatalytic process when natural water was employed. Photocatalytic efficiencies when ultrapure water was used seem to point out that surface area was not a prerequisite for the photodegradation of the selected mixture of pesticides. On the other hand, significant differences in total organic carbon (TOC) conversions were obtained with the two studied water compositions. On one side, Evonik materials appear to be mostly inhibited when natural water was employed, whereas on the other, it should be remarked that anatase Sigma-Aldrich (SA) and, particularly, Hombikat UV100 (HBK) materials presented a very limited photo-efficiency inhibition or even a higher initial rate of TOC removal when a natural water matrix was used, probably due to their specific surface properties (PZC, S BET). Therefore, heterogeneous photocatalysis has proved to be a promising technology for the degradation of the selected mixture of pesticides where the final photo-efficiency of the five commercial titania catalysts studied here responds to a complex balance between its surface and structural properties.