RESUMO
In this study, the interlaminar fracture toughness and impact strength of polyethersulfone reinforced with continuous carbon fibers were studied. Interlaminar fracture toughness tests were performed using the double cantilever beam method. It was shown that surface modification using the thermal oxidation method of the carbon fibers can strongly increase the interlaminar fracture toughness of the obtained composites. Thus, the maximum value reached 1.72 kJ/m2, which was 40% higher than the fracture toughness of the composites reinforced with initial carbon fibers. Moreover, fractographic analysis using a scanning electron microscope allowed us to highlight the main reasons for the dependence of fracture toughness on fiber content and surface modification conditions of the carbon fibers. It was shown that the main factor that allowed for an increase in fracture toughness was the enhanced interfacial interaction between the fibers and polymer matrix. Additionally, it was found that expectedly, there was a good correlation between interlaminar fracture toughness and interlaminar shear strength results. However, a negative influence of surface modification on the impact properties of composites was found. Such behavior occurred because of higher structural stability and lower exposure to delamination in multiple layers of the composites reinforced with the modified carbon fibers. It was found that impact energy reached ~150 kJ/m2 for the polyethersulfone-based composites reinforced with initial fibers, while the composites reinforced with modified carbon fibers showed impact energy values of only ~80 kJ/m2. Nevertheless, surface modification of carbon fibers using the thermal oxidation method can be an effective method for improving the performance properties of polyethersulfone-based composite materials.
RESUMO
In this study, the mechanical and thermophysical properties of carbon fiber-reinforced polyethersulfone are investigated. To enhance the interfacial interaction between carbon fibers and the polymer matrix, the surface modification of carbon fibers by thermal oxidation is conducted. By means of AFM and X-ray spectroscopy, it is determined that surface modification changes the morphology and chemical composition of carbon fibers. It is shown that surface modification dramatically increases the mechanical properties of the composites. Thus, flexural strength and the E-modulus of the composites reinforced with modified fibers reached approximately 962 MPa and 60 GPa, respectively, compared with approximately 600 MPa and 50 GPa for the composites reinforced with the initial ones. The heat deflection temperatures of the composites reinforced with the initial and modified fibers were measured. It is shown that composites reinforced with modified fibers lose their stability at temperatures of about 211 °C, which correlates with the glass transition temperature of the PES matrix. The thermal conductivity of the composites with different fiber content is investigated in two directions: in-plane and transverse to layers of carbon fibers. The obtained composites had a relatively high realization of the thermal conductive properties of carbon fibers, up to 55-60%.
RESUMO
The effect of thermal treatment of glass fibers (GF) on the mechanical and thermo-mechanical properties of polysulfone (PSU) based composites reinforced with GF was investigated. Flexural and shear tests were used to study the composites' mechanical properties. A dynamic mechanical analysis (DMA) and a heat deflection temperature (HDT) test were used to study the thermo-mechanical properties of composites. The chemical structure of the composites was studied using IR-spectroscopy, and scanning electron microscopy (SEM) was used to illustrate the microstructure of the fracture surface. Three fiber to polymer ratios of initial and preheated GF composites (50/50, 60/40, 70/30 (wt.%)) were studied. The results showed that the mechanical and thermo-mechanical properties improved with an increase in the fiber to polymer ratio. The interfacial adhesion in the preheated composites enhanced as a result of removing the sizing coating during the thermal treatment of GF, which improved the properties of the preheated composites compared with the composites reinforced with initial untreated fibers. The SEM images showed a good distribution of the polymer on the GF surface in the preheated GF composites.
RESUMO
Carbon fabrics are widely used in polymer based composites. Nowadays, most of the advanced high-performance composites are based on thermosetting polymer matrices such as epoxy resin. Thermoplastics have received high attention as polymer matrices due to their low curing duration, high chemical resistance, high recyclability, and mass production capability in comparison with thermosetting polymers. In this paper, we suggest thermoplastic based composite materials reinforced with carbon fibers. Composites based on polysulfone reinforced with carbon fabrics using polymer solvent impregnation were studied. It is well known that despite the excellent mechanical properties, carbon fibers possess poor wettability and adhesion to polymers because of the fiber surface chemical inertness and smoothness. Therefore, to improve the fiber-matrix interfacial interaction, the surface modification of the carbon fibers by thermal oxidation was used. It was shown that the surface modification resulted in a noticeable change in the functional composition of the carbon fibers' surface and increased the mechanical properties of the polysulfone based composites. Significant increase in composites mechanical properties and thermal stability as a result of carbon fiber surface modification was observed.