RESUMO
In the present study, the characteristics of leachate generated from dumpsite called 'Zapote' located in southern region of Tamaulipas, Mexico were evaluated. The adsorption of non-biodegradable organic matter measured as chemical oxygen demand (COD), color and heavy metals from leachate on activated carbon (AC) prepared in acid media from Guadua amplexifolia bamboo has been studied. In addition, the computation of kinetic parameters during the adsorption process as well as the most probable mechanisms was determined. The ACs were analyzed by using scanning electron microscopy and Fourier transform infrared spectroscopy. The experimental data showed that the ACs removed up to 81.4% of color and reduced COD up to 91.6% after 9â h of reaction at 60°C. For heavy metals, the maximum adsorption uptake was achieved at pH = 8.0 within 20â min with removal percentages of 87.0% (Pb(II)), 43.0% (Cu(II)) and 30.5% (Ni(II)). A pseudo-second-order model explained the adsorption kinetics most effectively for Pb, Ni and Cu, while a pseudo-first order was found for Zn. The AC synthesized from the G. amplexifolia species could be potentially used as an effective adsorbent in the reduction of COD, and removal of color and heavy metals.
Assuntos
Metais Pesados , Poluentes Químicos da Água , Adsorção , Carvão Vegetal , Cinética , MéxicoRESUMO
This work provides a comparative study on the corrosion protection efficiency of Ce, La films as well as Ce/La and La/Ce oxide bilayered coatings deposited onto AA7075 and AA6061 substrates by the radio frequency (RF) magnetron sputtering technique. The coating thickness ranged approximately from 12 to 835 nm, which changed with the deposition parameters and substrate composition. The relationship between microstructure, roughness and electrochemical performance is examined. The reactivity and crystallinity of rare earth (RE) films can be tailored by adjusting the sputtering parameters. Sputtered La films with thickness ca. 390 nm and average roughness of 66 nm showed the best corrosion protection properties in chloride medium as determined by potentiodynamic curves and electrochemical impedance spectroscopy (EIS). The method to obtain RE bilayered coatings, i.e., La/Ce or Ce/La as well as the substrate composition and applied power conditioned their inhibition properties. The RE bilayered coatings displayed better barrier properties than Ce films, which were poorer than those featured by La films.
RESUMO
This work reports the effect of different amounts of ceria nanoparticles on UV resistance and barrier properties of water-based polyurethane (WPU) on glass and AA7075 aluminum alloy substrates. Hybrid coatings were synthesized from an aliphatic WPUâ»HDI (1,6-hexamethylene di-isocyanate) and cerium oxide nanoparticles (CeO2) with an average particle size distribution of about 25 nm. Different nanoceria amounts (1, 3 and 5 wt %), mixing times (30, 60 and 120 min) and methods to disperse the nanostructures into the polymer matrix (magnetic stirring and sonication) were evaluated. Initially, the dispersion of CeO2 nanoparticles embedded in the polymer matrix and displacement in the corrosion potential (Ecorr) were analyzed by confocal scanning laser microscopy (CLSM) and open circuit potential (Eocp) measurements. According to this behavior, the dispersion and water ratio required during the polymerization process were established. Coated samples obtained after the second stage were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and optical light microscopy. In addition, optical measurements on glass substrates were evaluated with UV-vis spectroscopy. The effect of the synthesis parameters on the corrosion behavior of WPUâ»CeO2/AA7075 systems was investigated with Eocp and electrochemical impedance spectroscopy (EIS) in a 3 wt % NaCl solution. In addition, the films were subjected to 180 h of accelerated weathering. The results show that the combination of specific nanoceria addition with the optimal synthesis parameters enhances optical transparence of WPU as well as barrier properties. From these, the coated specimens prepared with 3 wt % of ceria content and sonicated for 30 min showed a highly dispersed system, which results in a high charge transfer resistance. The observed properties in clear coats deposited on metallic substrates suggested an improvement in the appearance and less deterioration in UV exposure in comparison with pure WPU, enhancing the protective properties of the AA7075 aluminum alloy when exposed to a corrosive medium.