The spectral reflection (specular and diffuse) and transmission of Columbia Resin 39 (CR-39) were measured for incoherent light with wavelengths in the range of 200-2500 nm. These results will be of use for the optical characterization of CR-39, as well as in investigations of the chemical modifications of the polymer caused by ultraviolet (UV) exposure. A Varian Cary 5000 was used to perform spectroscopy on several different thicknesses of CR-39. With proper analysis for the interdependence of reflectance and transmittance, results are consistent across all samples. The reflectivity from each CR-39-air boundary reveals an increase in the index of refraction in the near-UV. Absorption observations are consistent with the Beer-Lambert law. Strong absorption of UV light of wavelength shorter than 350 nm suggests an optical band gap of 3.5 eV, although the standard analysis is not conclusive. Absorption features observed in the near infrared are assigned to molecular vibrations, including some that are new to the literature.
RESUMO
We report an experimental investigation of the two-dimensional J_{eff}=1/2 antiferromagnetic Mott insulator by varying the interlayer exchange coupling in [(SrIrO_{3})_{1}, (SrTiO_{3})_{m}] (m=1, 2 and 3) superlattices. Although all samples exhibited an insulating ground state with long-range magnetic order, temperature-dependent resistivity measurements showed a stronger insulating behavior in the m=2 and m=3 samples than the m=1 sample which displayed a clear kink at the magnetic transition. This difference indicates that the blocking effect of the excessive SrTiO_{3} layer enhances the effective electron-electron correlation and strengthens the Mott phase. The significant reduction of the Néel temperature from 150 K for m=1 to 40 K for m=2 demonstrates that the long-range order stability in the former is boosted by a substantial interlayer exchange coupling. Resonant x-ray magnetic scattering revealed that the interlayer exchange coupling has a switchable sign, depending on the SrTiO_{3} layer number m, for maintaining canting-induced weak ferromagnetism. The nearly unaltered transition temperature between the m=2 and the m=3 demonstrated that we have realized a two-dimensional antiferromagnet at finite temperatures with diminishing interlayer exchange coupling.