Wet chemical synthesis and self-assembly of SnS2 nanoparticles on TiO2 for quantum dot-sensitized solar cells.

SnS2 nanoparticles were synthesized through a simple wet chemical process at room temperature. The SnS2 nanoparticles were approximately spherical in shape and had diameter about 3-4 nm. SnS2-sensitized TiO2 electrodes were fabricated by the immersion of chemically modified TiO2 to well-dispersed SnS2 solution for 72 h (i.e., self-assembly method.) SnS2-sensitized TiO2 electrodes were applied in quantum dot-sensitized solar cells (QDSSCs). Under AM1.5 irradiation with 100 mW/cm2 light intensity (at 1 sun), the short-circuit current density (J(sc)), the open-circuit voltage (V(oc)), the fill factor (FF), and the energy conversion efficiency (eta) were 0.47 mA/cm2, 0.29 V, 0.58 and 0.081%, respectively.

Synthesis of SnS nanoparticles by SILAR method for quantum dot-sensitized solar cells.

SnS-sensitized TiO2 electrodes were applied in quantum dot-sensitized solar cells (QDSSCs) which are environmentally more favorable than conventional Cd or Pb-chalcogenide-sensitized electrodes. SnS nanoparticles were well-distributed over the surface of TiO2 nanoparticles by the successive ionic layer adsorption and reaction (SILAR) method. Deposited SnS nanoparticles had diameter about 3 nm. Under AM1.5 irradiation with 100 mW/cm2 light intensity (at 1 sun), the energy conversion efficiency of obtained cells reached a value of 0.21% (0.25 cm2) at SILAR coating cycles of 5. In addition, the photovoltaic performance was improved by additional ZnS coating on the surface of SnS-sensitized TiO2 electrodes.