ACS Appl Mater Interfaces ; 15(15): 19715-19729, 2023 Apr 19.
Artigo em Inglês | MEDLINE | ID: mdl-37029740

RESUMO

The anti-friction of diamond-like carbon (DLC) is achieved by a well-developed carbonaceous transfer layer, and Ti-doped DLC is developed into a robustly built-up carbonaceous transfer layer. The friction performance of DLC depends on the operating environment, e.g., ambient gas, humidity, temperature, lubricants, and mating material. In this study, we aimed to reveal the environmental sensitivities of Ti-DLC on friction characteristics. To this end, a Ti-DLC was rubbed against a steel ball, and friction behaviors were evaluated with different gas compositions, humidity, and temperature. Finally, we identified that fractional coverage of water on surfaces affected the anti-graphitization on Ti-DLC, leading to avoiding friction reduction.

2.
Langmuir ; 37(12): 3563-3574, 2021 Mar 30.
Artigo em Inglês | MEDLINE | ID: mdl-33730499

RESUMO

In the ceramic industry, ceramic particles remain on a mold surface due to which the mold requires frequent cleaning during press molding, reducing productivity. Surface texturing and tetrahedral amorphous carbon (ta-C) coatings are well-known surface-energy controllable treatments developed for low adhesion, low friction, and high wear resistance. In the present paper, we demonstrate the effect of reducing ceramic residues using nanotexturing, ta-C coatings, and their combination. We compare two surface morphologies (i.e., 770 nm pitch nanotexturing and flat) and five materials (i.e., nonhardened steel, hardened steel, ta-C, and two types of nitrogen-doped ta-C (ta-CNx). Molding test results show that the ta-C coating on flat surfaces with the highest hardness of 30 GPa shows the lowest residual amount of 5.9 µg for Al2O3 ceramic particles. The amount is 82% less than that of the nonhardened steel. The ta-CNx20, made with a nitrogen flow rate of 20 sccm, shows the lowest residual amount of 234 µg for SiO2 ceramic particles, which is 81% less than that of the nontextured ta-CNx20. In conclusion, we provide design guidelines for nanotextured mold surfaces including the texturing pitch should be small enough for ceramic particles; the mold surface should be sufficiently hard; the lower the surface energy per unit area, the less residues of ceramic particles.

3.
Nano Lett ; 7(11): 3285-9, 2007 Nov.
Artigo em Inglês | MEDLINE | ID: mdl-17929874

RESUMO

Characteristic tribological properties, such as nonlinearity of the friction force-normal load curve, high coefficient of friction, and good wear-resistant performance were observed on densely packed, vertically aligned carbon nanotubes (CNTs) with different diameters and lengths using atomic force microscopy. Shorter and thicker CNTs were found to have higher coefficients of friction. The observed properties were attributed to the nonlinear elastic property of the CNTs caused by buckling.