Effect of Stacking Sequence on Long-Term Creep Performance of Pultruded GFRP Composites.

Pultruded glass-fibre reinforced polymer (pGFRP) composites are classified as lightweight material, which exhibit high strength-to-weight ratio for structural usage. This composite material has been applied as cross-arm members in transmission towers due to its ability in thermal and electrical insulation. However, the influence of the stacking sequence of pGFRP composite on its mechanical performance has not been fully covered in the literature to explain the long-term durability of the current cross-arm designs. The study expected to evaluate five fiber layers with various stacking sequences in terms of quasi-static and creep tests in a four-point bending mode. The creep test was performed for 1440 h (60 days). These composites were fabricated using the pultrusion process in the form of a square hollow structure. Later, it was cut into composite coupons with various sizes depending on the test conducted. The results showed that nine layers with 0°/45°/0°/-45°/0°/-45°/0°/45°/0° had the ultimate flexural strength. This stacking sequence configurations seemed to be optimally manufactured in continuous roving fibre by alternating between 0° and ±45° fiber orientations. Additionally, the S-9 pGFRP composite sample showed that it had a low-creep deflection with high elastic and apparent creep moduli in 1440 h. In terms of strength reduction factor, this configuration was recorded as the highest. The findings showed that the nine layers of pGFRP composites with alternation of 0° and ±45° fiber orientations were highly suitable for structural application at transmission towers for a long-term operation.

Sugar Palm Fibre-Reinforced Polymer Composites: Influence of Chemical Treatments on Its Mechanical Properties.

In the era of globalisation, decreasing synthetic resources, especially petroleum, have encouraged global communities to apply biomass waste as a substitute material for green technology development. The development of plastic products from lignocellulosic fibre-reinforced composites has been a hot topic among material scientists and engineers due to their abundance, sustainable in nature, and less toxic towards health. For the Malaysian scenario, sugar palm is a plant found in the wild and locally planted in certain areas in Malaysia and Indonesia. Generally, sugar palm can be harvested for traditional foods, fruits, starch sugar (gula kabung), and alcohol, whereas sugar palm fibre (SPF) is used in conventional products (brushes and brooms). Various researchers are working on the characterisation of fibre and its composites for engineering and packaging products. The main drawback of SPF is its hydrophilic behaviour, which leads to high moisture uptake and inhibits a good bond between the fibre and the matrix. Thus, a solution for this problem is by implementing chemical treatments on the fibre. From the literature review, no comprehensive review paper has been published on the influence of chemical treatment on the mechanical behaviour of SPF-reinforced polymer composites. Thus, the present review examines recent studies on the mechanical properties of sugar palm lignocellulosic fibres with various chemical treatments to evaluate their potential in structural applications.

Flexural Creep Behaviour of Pultruded GFRP Composites Cross-Arm: A Comparative Study on the Effects of Stacking Sequence.

Pultruded glass fibre reinforced polymer (pGFRP) composites provide outstanding properties for composite polymer cross arms in power transmission line applications. This study has investigated the effects of various stacking sequences of fibres directions of pGFRP on flexural strength and creep behaviour. The use of static four-point bending flexural tests revealed that Stacking Sequence 2 (±45/0/90/0/90/0) had a significant flexural strength of 399.9 MPa while Stacking Sequence 1 (±45/90/0/±45) had a flexural strength of 242.5 MPa. Furthermore, the four-point bending creep experiments were performed at three distinct stress levels, notably 12%, 24%, and 37% of the ultimate flexural strength, to characterise the creep behaviour of distinct stacking sequences. Moreover, Findley's power law equation for bending creep behaviour has revealed that the time-dependent reduction factor of Stacking Sequence 1 and Stacking Sequence 2 estimates a drop in flexural modulus of 23% and 10% respectively.