RESUMO
Corn starch-based nanocomposite films usually have low moisture barrier properties. Adding virgin coconut oil (VCO) as a hydrophobic component can improve the nanocomposite film's characteristics, especially the film's permeability and elongation properties. This study aimed to determine the role of VCO with various concentrations (0, 3, 5 wt%) on the physical, mechanical, and water vapor transmission characteristics of corn starch/NCC-based nanocomposite films. Adding 3% VCO to the film showed the lowest WVTR value by 4.721 g/m2.h. At the same time, the value of tensile strength was 4.243 MPa, elongation 69.28%, modulus of elasticity 0.062 MPa, thickness 0.219 mm, lightness 98.77, and water solubility 40.51%. However, adding 5 wt% VCO to the film increased the film's elongation properties by 83.87%. The SEM test showed that adding VCO formed a finer structure with pores in several areas. The FTIR films showed that adding VCO caused a slightly higher absorption peak shift at the O-H groups and new absorption peaks at wave numbers 1741 cm-1 and 1742 cm-1. The results of this study may provide opportunities for the development of nanocomposite films as biodegradable packaging in the future.