Facile fabrication of arecanut palm sheath based robust hydrophobic cellulose nanopapers via self-assembly of ZnO nanoflakes and its shelf-life prediction for sustainable packaging applications.

Cellulose nanofibers have been extracted from arecanut palm sheath fibers via mild oxalic acid hydrolysis coupled with steam explosion technique. Cellulose nanofibers with diameter of 20.23 nm were obtained from arecanut palm sheath fibers. A series of robust hydrophobic cellulose nanopapers were fabricated by combining the synergistic effect of surface roughness induced by the successful deposition of zinc oxide (ZnO) nanoflakes and stearic acid modification via a simple and cost-effective method. In this work, agro-waste arecanut palm sheath was employed as a novel source for the extraction of cellulose nanofibers. 2 wt% of ZnO nanoflakes and 1 M concentration of stearic acid were used to fabricate mechanically robust hydrophobic cellulose nanopapers with a water contact angle (WCA) of 134°. During the deposition of zinc oxide nanoflakes on the CNP for inducing surface roughness, a hydrogen bonding interaction is formed between the hydroxyl groups of cellulose nanofibers and the zinc oxide nanoflakes. When this surface roughened CNP was dipped in stearic acid solution. The hydroxyl groups in zinc oxide nanoflakes undergoes esterification reaction with carboxyl groups in stearic acid solution forming an insoluble stearate layer and thus inducing hydrophobicity on CNP. The fabricated hydrophobic cellulose nanopaper displayed a tensile strength of 22.4 MPa and better UV blocking ability which is highly desirable for the sustainable packaging material in the current scenario. Furthermore, the service life of the pristine and modified cellulose nanopapers was predicted using the Arrhenius equation based on the tensile properties obtained during the accelerated ageing studies. The outcome of this study would be broadening the potential applications of hydrophobic and mechanically robust cellulose nanopapers in sustainable packaging applications.

Mechanical and Water Uptake Properties of Epoxy Nanocomposites with Surfactant-Modified Functionalized Multiwalled Carbon Nanotubes.

The superior mechanical properties of multi-walled carbon nanotubes (MWCNTs) play a significant role in the improvement of the mechanical and thermal stability of an epoxy matrix. However, the agglomeration of carbon nanotubes (CNTs) in the epoxy is a common challenge and should be resolved to achieve the desired enhancement effect. The present paper investigated the thermal, mechanical, and water uptake properties of epoxy nanocomposites with surfactant-modified MWCNTs. The nanocomposites were prepared through the incorporation of different weight concentrations of MWCNTs into the epoxy matrix. Comparative analysis of neat epoxy and epoxy/CNT nanocomposites were conducted through thermal, mechanical, microscopic, and water uptake tests to reveal the improvement mechanism. The homogenous distribution of the CNTs in the epoxy was achieved by wrapping the surfactant onto the CNTs. The addition of surfactant-modified CNTs into the epoxy caused an obvious increase in the mechanical and thermal properties. This improvement mechanism could be attributed to the uniform dispersion of the CNTs in the epoxy matrix reducing the free volume between the polymer chains and restricting the chain segmental mobility, leading to strong interfacial bonding and an efficient load transfer capability between the CNTs and the epoxy matrix. However, the mechanical and thermal properties of the epoxy/CNT nanocomposite decreased owing to the agglomeration effect when the concentration of the CNTs exceeded the optimal percentage of 1.5%. Additionally, the CNTs could impart a reduction in the wettability of the surface of the epoxy/CNT nanocomposite, leading to the increase in the contact angle and a reduction in the water uptake, which was significant to improve the durability of the epoxy. Moreover, the higher weight concentration (2%) of the CNTs showed a greater water uptake owing to agglomeration, which may cause the formation of plenty of microcracks and microvoids in the nanocomposite.

Durability of an Epoxy Resin and Its Carbon Fiber- Reinforced Polymer Composite upon Immersion in Water, Acidic, and Alkaline Solutions.

The usage of polymer composites in various engineering fields has increased. However, the long-term service performance of such materials under aggressive conditions is still poorly understood, which limits the development of safe and economically effective designs. In this study, the aging of an epoxy resin and its carbon fiber-reinforced polymer (CFRP) composites upon immersion in water, acidic, and alkaline solutions was evaluated at different temperatures. The service life of the CFRP composites under various conditions could be predicted by the Arrhenius theory. The thermal and mechanical analysis results indicated that the CFRP composites were more vulnerable to HCl owing to the higher moisture absorption and diffusion of HCl into their cracks. The scanning electron microscopy results showed that the polymer matrix was damaged and degraded. Therefore, to allow long-term application, CFRP composites must be protected from acidic environments.