RESUMO
Herein, we reports the application of various spinel ferrite nanoparticles, MFe2O4 (M = Co, Ni, Cu, Zn), as efficient catalyst for Biginelli reaction. All ferrite nanoparticles were synthesized using a novel aqueous solution based method. It was observed that, the catalytic activity of the ferrite nanoparticles followed the decreasing order of CoFe2O4 > CuFe2O4 > NiFe2O4 > ZnFe2O4. The most important feature of these ferrite nanocatalysts is that, these nanoparticles can directly be used as catalyst and no surface modification or functionalization is required. These ferrite nanoparticles are easily separable from reaction mixture after reaction by using a magnet externally. Easy synthesis methodology, high catalytic activity, easy magnetic separation and good reusability make these ferrite nanoparticles attractive catalysts for Biginelli reaction.
RESUMO
The gel to carbonate precipitate route has been used for the synthesis of Ni1-xZnxFe2O4 (x = 0, 0.25, 0.5 and 0.75) bulk inverse spinel ferrite powder samples. The optimal zinc (50%) substitution has shown the maximum saturation magnetic moment and resulted into the maximum magnetic loss tangent (tanδm) > -1.2 over the entire 2-10 GHz frequency range with an optimum value ~-1.75 at 6 GHz. Ni0.5Zn0.5Fe2O4- Acrylo-Nitrile Butadiene Rubber (NBR) composite samples are prepared at different weight percentage (wt%) of ferrite loading fractions in rubber for microwave absorption evaluation. The 80 wt% loaded Ni0.5Zn0.5Fe2O4/NBR composite (FMAR80) sample has shown two reflection loss (RL) peaks at 5 and 10 GHz. Interestingly, a single peak at 10 GHz for 3.25 mm thickness, can be scaled down to 5 GHz by increasing the thickness up to 4.6 mm. The onset of such twin matching frequencies in FMAR80 composite sample is attributed to the spin resonance relaxation at ~5 GHz (fm1) and destructive interference at λm/4 matched thickness near ~10 GHz (fm2) in these composite systems. These studies suggest the potential of tuning the twin frequencies in Ni0.5Zn0.5Fe2O4/NBR composite samples for possible microwave absorption applications.
RESUMO
In this paper, we report a simple but novel aqueous solution based 'one-pot' method for preparation of (NiFe2O4)x-(SrFe12O19)1-x nanocomposites consist of hard ferrite-soft ferrite phases. A physical mixing method has also been employed to prepare nanocomposites having same compositions. The effects of synthetic methodologies on the microstructures of the nanocomposites as well as their magnetic and microwave absorption properties have been evaluated. Crystal structures and microstructures of these composites have been investigated by using X-ray diffraction, transmission electron microscope and scanning electron microscope. In the nanocomposites, prepared by both methods, presence of nanocrystalline NiFe2O4 and SrFe12O19 phases was detected. However, nanocomposites, prepared by one-pot method, possessed better homogeneous distribution of hard and soft ferrite phases than the nanocomposites, prepared by physical mixing method. Nanocomposites, prepared by one-pot method, demonstrated significant spring exchange coupling interaction between hard and soft ferrite phases and exhibited magnetically single phase behaviour. The spring exchange coupling interaction enhanced the magnetic properties (high saturation magnetization and coercivity) and microwave absorption properties of the nanocomposites, prepared by one-pot method, in comparison with the nanocomposites prepared by physical mixing method as well as pure NiFe2O4 and SrFe12O19 nanoparticles. Minimum reflection loss of the composite was ~ -17 dB (i.e., 98% absorption) at 8.2 GHz for an absorber thickness of 3.2 mm.