Fatigue Failure Load of a Bonded Simplified Monolithic Feldspathic Ceramic: Influence of Hydrofluoric Acid Etching and Thermocycling.

OBJECTIVE: To evaluate the effect of hydrofluoric acid (HF) etching and thermocycling (Tc) on fatigue failure load of feldspathic ceramic restorations cemented with two resin cements. METHODS: Disc-shaped feldspathic ceramic (Vitablocs Mark II; Ø=10 mm, 1.0-mm thick) and G10 epoxy resin (Ø=10 mm, 2.5-mm thick) specimens were made and randomly allocated considering three factors: ceramic etching (ie, with vs without 10% HF plus silane application), resin cement (ie, self-adhesive [RelyX U200; U200] or conventional [Multilink Automix; MA]), and Tc (ie, with vs without 5-55°C/12,000 cycles). Adhesive cementation followed each manufacturer's instructions. The fatigue test (n=20) was based on the staircase approach (250,000 cycles; 20 Hz). Contact angle, surface topography, and fractography analysis were also executed. Specific statistical tests were employed for each outcome (α=0.05). RESULTS: The interaction of HF and Tc factors decreased the fatigue resistance for both cements (U200 542.63>U200/HF-Tc 495.00; MA 544.47>MA/HF-Tc 506.84). Comparing the cements associated with HF or Tc, there was statistical superiority for MA (U200-Tc 537.37