RESUMO
Yttria-stabilized zirconia (YSZ) is well-known as a material with perfect mechanical, thermal, and electrical properties. It is used for manufacturing various high-temperature components for aerospace and energy generation, as well as wear- and corrosion-resistant devices in medicine. This work investigated the effect of a Y2O3 addition to ZrO2 on the microstructure and mechanical properties of YSZ ceramics produced by one sintering schedule. ZrO2 ceramics doped with 3, 4, 5, 6, 7, and 8 mol% Y2O3 (designated 3YSZ through to 8YSZ) were prepared by using conventional sintering at 1550 °C for 2 h in argon. The effect of yttria content was analyzed with respect to grain size, morphology of the microstructural features, phase composition, parameters of fracture surface, and flexural strength. The 7YSZ ceramics sintered at 1550 °C for 2 h showed the highest level of flexural strength due to the formation of the fine-grained microstructure containing mainly the monoclinic and tetragonal zirconia phases. The fracture micromechanism in the studied YSZ ceramics is discussed.
RESUMO
It is known that the yttria-stabilized zirconia (YSZ) material has superior thermal, mechanical, and electrical properties. This material is used for manufacturing products and components of air heaters, hydrogen reformers, cracking furnaces, fired heaters, etc. This work is aimed at searching for the optimal sintering mode of YSZ ceramics that provides a high crack growth resistance. Beam specimens of ZrO2 ceramics doped with 6, 7, and 8 mol% Y2O3 (hereinafter: 6YSZ, 7YSZ, and 8YSZ) were prepared using a conventional sintering technique. Four sintering temperatures (1450 °C, 1500 °C, 1550 °C, and 1600 °C) were used for the 6YSZ series and two sintering temperatures (1550 °C and 1600 °C) were used for the 7YSZ and 8YSZ series. The series of sintered specimens were ground and polished to reach a good surface quality. Several mechanical tests of the materials were performed, namely, the microhardness test, fracture toughness test by the indentation method, and single-edge notch beam (SENB) test under three-point bending. Based on XRD analysis, the phase balance (percentages of tetragonal, cubic, and monoclinic ZrO2 phases) of each composition was substantiated. The morphology of the fracture surfaces of specimens after both the fracture toughness tests was studied in relation to the mechanical behavior of the specimens and the microstructure of corresponding materials. SEM-EDX analysis was used for microstructural characterization. It was found that both the yttria percentage and sintering temperature affect the mechanical behavior of the ceramics. Optimal chemical composition and sintering temperature were determined for the studied series of ceramics. The maximum transformation toughening effect was revealed for ZrO2-6 mol% Y2O3 ceramics during indentation. However, in the case of a SENB test, the maximum transformation toughening effect in the crack tip vicinity was found in ZrO2-7 mol% Y2O3 ceramics. The conditions for obtaining YSZ ceramics with high fracture toughness are discussed.