Metal Knitting: A New Strategy for Cold Gas Spray Additive Manufacturing.

Cold Spray Additive Manufacturing (CSAM) is an emergent technique to produce parts by the additive method, and, like other technologies, it has pros and cons. Some advantages are using oxygen-sensitive materials to make parts, such as Ti alloys, with fast production due to the high deposition rate, and lower harmful residual stress levels. However, the limitation in the range of the parts' geometries is a huge CSAM con. This work presents a new conceptual strategy for CSAM spraying. The controlled manipulation of the robot arm combined with the proper spraying parameters aims to optimize the deposition efficiency and the adhesion of particles on the part sidewalls, resulting in geometries from thin straight walls, less than 5 mm thick, up to large bulks. This new strategy, Metal Knitting, is presented regarding its fundamentals and by comparing the parts' geometries produced by Metal Knitting with the traditional strategy. The Metal Knitting described here made parts with vertical sidewalls, in contrast to the 40 degrees of inclination obtained by the traditional strategy. Their mechanical properties, microstructures, hardness, and porosity are also compared for Cu, Ti, Ti6Al4V, 316L stainless steel, and Al.

Evaluation of cavitation/corrosion synergy of the Cr3C2-25NiCr coating deposited by HVOF process.

Wear processes are always present in components exposed to different work situations. Hydraulic turbines in electric power generation and ship propellers are good examples of components subject to wear and corrosion. One way to protect these components, for example, is the deposition of coatings by thermal spray processes. Indeed, there are several wear or corrosion mechanisms acting simultaneously, and the validation of the mechanisms separately, is not the best way to select the better material. When materials have passivation as protective mechanism against corrosion, the mass loss due erosion can affect the materials selection. This paper study the combined effect of the corrosion on the cavitation mass loss, as well as, the cavitation mass loss influence on the corrosion properties of a chromium carbide Cr3C2-25NiCr coating. Despite of the modification of the erosion mechanism on the cavitated samples under 3,5% NaCl solution, the volume loss did not show any significant alteration. Cavitation mass loss increase the corrosion process, reducing significantly the corrosion potential and raising the corrosion current. It was observed that the cavitation of the Cr3C2-25NiCr HVOF coating influences much more the corrosion kinetics, than the corrosion affects the cavitation resistance.