RESUMO
The fabrication of instructive materials to engineer bone substitute scaffolds is still a relevant challenge. Current advances in additive manufacturing techniques make possible the fabrication of 3D scaffolds with even more controlled architecture at micro- and submicrometric levels, satisfying the relevant biological and mechanical requirements for tissue engineering. In this view, integrated use of additive manufacturing techniques is proposed, by combining 3D printing and air-jet spinning techniques, to optimize the fabrication of PLA tubes with nanostructured fibrous coatings for long bone defects. The physicochemical characterization of the 3D tubular scaffolds was performed by scanning electron microscopy, thermogravimetric analysis, differential scanning calorimetry, profilometry, and mechanical properties. In vitro biocompatibility was evaluated in terms of cell adhesion, proliferation, and cell-material interactions, by using human fetal osteoblasts to validate their use as a bone growth guide. The results showed that 3D-printed scaffolds provide a 3D architecture with highly reproducible properties in terms of mechanical and thermal properties. Moreover, nanofibers are collected onto the surface, which allows forming an intricate and interconnected network that provides microretentive cues able to improve adhesion and cell growth response. Therefore, the proposed approach could be suggested to design innovative scaffolds with improved interface properties to support regeneration mechanisms in long bone treatment.
RESUMO
This study evaluated the influence in the biocompatibility of human periodontal ligament (hPDL) mesenchymal stromal cell onto poly lactic-acid (PLA) films and PLA fiber membrane. Fiber scaffold was prepared via air jet spinning (AJS) from PLA solutions (6, 7, and 10%) and analyzed using SEM, AFM and FTIR. Biocompatibility was evaluated by adhesion, proliferation and cell-material interaction. PLA film exhibited a smooth and homogenously surface topography in comparison with random orientation of PLA fiber with roughness structure where diameter size depends on PLA solution. Moreover, cell adhesion; proliferation and cell-material interaction has the best respond on random orientation nanofiber of 10, followed by 7, and 6% of PLA in comparison with PLA films. It could be concluded that AJS is an attractive alternative technique for manufacture fiber scaffolds with a tunable random orientation geometry of fibers that allow to produce interconnected porous formed by nanometric fiber diameter structures that could be a potential scaffold for periodontal tissue engineering applications.