Structure and Mechanical Properties of iPP-Based Nanocomposites Crystallized under High Pressure.

The unique nonparallel chain arrangement in the orthorhombic γ-form lamellae of isotactic polypropylene (iPP) results in the enhancement of the mechanical properties of γ-iPP. Our study aimed at the investigation of the mechanical properties of γ-iPP nanocomposites with 1-5 wt.% multiwall carbon nanotubes (MWCNT) and 5 wt.% organo-modified montmorillonite prepared by melt-mixing and high-pressure crystallization. Neat iPP and the nanocomposites were crystallized under high pressures of 200 MPa and 300 MPa, and for comparison under 1.4 MPa, in a custom-built high-pressure cell. The structure of the materials was studied using WAXS, SAXS, DSC, and SEM, whereas their mechanical properties were tested in plane-strain compression. Under a small pressure of 1.4 MPa, polymer matrix in all materials crystallized predominantly in the α-form, the most common monoclinic form of iPP, whereas under high pressure it crystallized in the γ-form. This caused a significant increase in the elastic modulus, yield stress, and stress at break. Moreover, due to the presence of MWCNT, these parameters of the nanocomposites exceeded those of the neat polymer. As a result, a 60-70% increase in the elastic modulus, yield stress, and stress at break was achieved by filling of iPP with MWCNT and high-pressure crystallization.

Semisolid extrusion 3D printing of Dolutegravir-Chitosan nanoparticles laden polymeric buccal films: personalized solution for pediatric treatment.

In this work, the semi solid extrusion 3D printing process was utilized to incorporate anti-HIV drug Dolutegravir and its nanoparticles into the buccal film (BF) that was fabricated using the developed polymer ink. The composite made of polyvinyl alcohol (PVA) and sodium alginate was processed into a 3D printing polymer ink with optimum viscosity (9587 ± 219 cP) needed for the seamless extrusion through the nozzle of the 3D printer. The formulated BFs were assessed for its physical properties like weight (0.414 ± 0.3 g), thickness (1.54 ± 0.02 mm), swelling index (18.5 ± 0.91%), and mucoadhesiveness strength (0.165 ± 0.09 N) etc, The structural integrity and the surface morphology of the developed BFs were investigated by scanning electron microscopy analysis. The chemical stability and the solid-state nature of the drug in the BFs were assessed by Fourier transform infrared and x-ray diffraction analysis respectively. Further the BFs were assessed for drug dissolutionin-vitroandex-vivo, to study the effect of polymer composition and printing condition on the dissolution profile of the drug in the simulated salivary fluid. The results demonstrated that the developed PVA based polymer ink for 3D printing utilizing pressure is a versatile approach in the context of manufacturing mucoadhesive BFs customized in terms of shape and the amount of drug loaded.

Crystallization of Isotactic Polypropylene Nanocomposites with Fibrillated Poly(tetrafluoroethylene) under Elevated Pressure.

Nanocomposites of isotactic polypropylene with 1-5 wt.% of fibrillated PTFE (PP/T) were prepared, and their crystallization during cooling under elevated pressure, in a wide pressure range, up to 300 MPa, as well as the resulting structure, were examined. The crystallization peak temperatures of PP/T, especially with 3 and 5 wt.% of PTFE, exceeded by up to 13 °C those of neat PP. Moreover, a fine-grain structure was formed in PP/T in the entire pressure range, which proved the ability of the fibrillated PTFE to nucleate crystallization of PP in the γ-form under elevated pressure. This also resulted in a higher crystallinity level developed in the γ-domain, before the temperature range of the α-domain was reached during cooling. Hence, the γ-content increased in comparison to that in neat PP, under the pressure up to 200 MPa, especially under 50-100 MPa.