Effect of the Structural and Morphological Properties of Surfactant-Assisted Hydroxyapatite on Dermal Irritation and Antibacterial Activity.

Hydroxyapatite (HAp) nanoparticles with a homogeneous rod morphology were successfully synthesized using the hydrothermal method. The powders were characterized using Fourier transform infrared spectroscopy, X-ray diffraction, and scanning electron microscopy. The antibacterial and dermal irritation analyses of the samples were performed and discussed. The use of cationic and anionic surfactants, namely, cetyltrimethylammonium bromide (CTAB) and sodium dodecyl sulfate (SDS), respectively, at a low concentration (2.5 mol%) modified the length/diameter (L/D) ratio of the HAp rods. Structural characterizations of hydroxyapatite synthesized without surfactant (HA), with 2.5 and 5 mol% of SDS (SDS- and SDS+, respectively), and with 2.5 and 5 mol% of CTAB (CTAB- and CTAB+, respectively) revealed well-crystallized samples in the hexagonal phase. The CTAB- sample presented antibacterial activity against Pseudomonas aeruginosa, Escherichia coli, Streptococcus anginosus, Staphylococcus aureus, Micrococcus luteus, and Klebsiella pneumoniae, suggesting that antimicrobial susceptibility was promoted by the bacterial nature and the use of the surfactant. Dermal irritation showed no clinical signs of disease in rabbits during the study, where there was neither erythema nor necrosis at the inoculation sites.

Luminescent Properties of (004) Highly Oriented Cubic Zinc Blende ZnO Thin Films.

Photoluminescence properties of cubic zinc blende ZnO thin films grown on glass substrates prepared by the spray pyrolysis method are discussed. X-ray diffraction spectra show the crystalline wurtzite with preferential growth in the (002) orientation and a metastable cubic zinc blende phase highly oriented in the (004) direction. Raman measurements support the ZnO cubic modification growth of the films. Photoluminescence (PL) spectra of zinc blende films are characterized by a new PL band centerd at 2.70 eV, the blue emission, in addition there are two principal bands that are also found in hexagonal ZnO films with the peak positions at 2.83 eV and 2.35 eV. The origin of the 2.70 eV band can be attributed to transitions from Zn-interstitial to Zn-vacancies. It is also important to mention that the PL intensity of the 2.35 eV band of the zinc blende thin films is relatively higher than in the band present in hexagonal ZnO films, which means that zinc blende films have more oxygen vacancies, as was corroborated by means of the energy dispersion spectroscopy (EDS) measurements. PL spectra at 77 °K were measured and the 2.70 eV band was confirmed for the zinc blende films. Some PL bands of cubic films also appeared for the hexagonal phase, which is due, to a certain extent, to the similar ions stacking of both wurtzite and zinc blende symmetries.