Effect of Fiber Sizing Levels on the Mechanical Properties of Carbon Fiber-Reinforced Thermoset Composites.

Fiber sizing is one of the most important components in manufacturing composites by affecting mechanical properties, including strength and stiffness. The sizing of manmade fibers offers many advantages, such as improving fiber/matrix adhesion and bonding properties, protecting fiber surfaces from damage during the processing and weaving stages, and enhancing the surface wettability of polymer matrices. In this work, the influence of fiber sizing levels on carbon fibers' (CFs) mechanical properties is reported at room temperature using single fiber tensile testing (Favimat+), single fiber pullout testing (SFPO), and interfacial elemental analysis by X-ray photoelectron spectroscopy (XPS). Standard modulus CFs (7 ± 0.2 µm in diameter) were sized using two commercially available Michelman sizing formulations. The average solid content for each sizing formulation was 26.3 ± 0.2% and 34.1 ± 0.2%, respectively. HEXION RIMR 135 with curing agent RIMH 137 was used as a model thermoset epoxy matrix during SFPO measurements. A predictive engineering fiber sizing methodology was also developed. Sizing amounts of 0.5, 1, and 2 wt.% on the fiber surface were achieved for both sizing formulations. For each fiber size level, 50 single-fiber tensile testing experiments and 20 single-fiber pull-out tests were conducted. The ultimate tensile strength (σult) of the carbon fibers and the interfacial shear strength (τapp) of the single fiber composite were analyzed. The sizing levels' effect on interfacial shear stress and the O/C (Oxygen/Carbon) surface composition ratio was investigated. Based on our experimental findings, an increase of 6% in fiber performance was recorded for ultimate tensile and interfacial shear strengths. As a result, generalized fiber sizing and characterization methods were established. These developed methods can be used to characterize the strength and interfacial shear strength of manmade fibers with different sizing formulations and solid contents irrespective of the matrix, i.e., thermoset or thermoplastic.

Electrolytic Surface Treatment for Improved Adhesion between Carbon Fibre and Polycarbonate.

To achieve good mechanical properties of carbon fibre-reinforced polycarbonate composites, the fibre-matrix adhesion must be dialled to an optimum level. The electrolytic surface treatment of carbon fibres during their production is one of the possible means of adapting the surface characteristics of the fibres. The production of a range of tailored fibres with varying surface treatments (adjusting the current, potential, and conductivity) was followed by contact angle, inverse gas chromatography and X-ray photoelectron spectroscopy measurements, which revealed a significant increase in polarity and hydroxyl, carboxyl, and nitrile groups on the fibre surface. Accordingly, an increase in the fibre-matrix interaction indicated by a higher interfacial shear strength was observed with the single fibre pull-out force-displacement curves. The statistical analysis identified the correlation between the process settings, fibre surface characteristics, and the performance of the fibres during single fibre pull-out testing.