Sustainable Alkaline Hydrolysis of Polyester Fabric at Low Temperature.

High crystallinity leads to low hydrophilicity of fabric made of (poly(ethylene terephthalate)) fibers (PET) causing problems in finishing, washing, and dyeing processes. To improve these properties, the surface of PET fibers is usually modified by hydrolysis. Alkaline hydrolysis is a conventional process usually performed at a temperature higher than 100 °C for more than 1 h. However, the use of strong alkali and high processing temperatures (>100 °C) can lead to fabric damage and a negative impact on the environment. Therefore, in this paper, the possibility of hydrolysis of the PET fibers in the fabric in a sustainable, energy-efficient process was researched. The influence of low temperature (60-100 °C) and an accelerator (a cationic surfactant HDTMAC) to PET alkaline hydrolysis was studied through weight loss, the loss in breaking force, and fiber morphology. The kinetics of PET dissolution in 1.5 mol cm-3 NaOH at low temperature with and without the addition of HDTMAC was determined and the activation energy was calculated according to the theoretical model. It has been confirmed that PET hydrolysis can be carried out in 1.5 mol cm-3 NaOH with the addition of HDTMAC as an accelerator at 80 °C for 10 min. This process is more economically and energetically acceptable than the conventional process, and is therefore more sustainable.

Carboxymethyl Cellulose and Carboxymethyl Starch as Surface Modifiers and Greying Inhibitors in Washing of Cotton Fabrics.

This research is focused on cellulose and starch derivatives, carboxymethyl cellulose (CMC) and carboxymethyl starch (CMS), added to the detergent in washing reference cotton fabric in soft and hard water at 40, 60 and 90 °C. The applied polymers were analyzed through the potential of surface cellulose modification and inhibition of stain transfer from standard stain donors to modified and initial cotton fabrics. The surface modification of the cotton fabrics, characterized by the zeta potential and amounts of deposits, was coupled with the cluster analysis as well as a whiteness assessment. The obtained results of the zeta potential and degree of whiteness of the reference cotton fabrics before and after washing showed differences between CMC and CMS. The appropriateness of the cluster analysis was confirmed in assessing the potential of applied polymers for surface modification of cotton fabrics and greying inhibition.