RESUMO
The removal of the surface paint of Q345 (Gr·B) steel, as well as microstructure and hardness of the cleaned surface were investigated. The laser source used in this study is a nanosecond pulsed Gaussian light source. The surface morphology and microstructure were characterized by a scanning electron microscope and electron back-scattered diffraction. A hardness test was used for capturing variations of the parameter of the cleaned region in comparison to the base metal. The results show that when the X-scanning speed was 1500 mm/s and Y-moving speeds was 7 mm/s during ns-laser cleaning, respectively, the cleaned surface was relatively flat and there was only a few small residual paint. In addition, the contents of Fe and C elements on the cleaned surface reached to 89% and 9%, respectively. Moreover, the roughness was the lowest of 0.5 µm through the observation of the three-dimensional topography. In addition, a fine grain layer appeared on the cleaned surface after laser cleaning at the X-scanning speeds of 500 mm/s and 1000 mm/s. The maximum hardness of the fine grain layer was more than 400 HV, higher than the base metal.