Cause of Color Modification in Tanzanite after Heat Treatment.

Natural tanzanites usually show strongly trichroic coloration from violet to blue, and brown colors in different directions. However, this characteristic is easily changed to violet-blue dichroism after heat treatment. Moreover, the cause of color modification after heating is still controversial. A few researchers have previously suggested that trace amounts of either vanadium or titanium substituted in aluminum site should be the main determinant of color after the heat treatment. Alteration of either V3+ to V4+ or Ti3+ to Ti4+ may relate to light absorption around 450-460 nm, which is the main cause. UV/vis/NIR absorption spectroscopy and X-ray absorption spectroscopy (XAS), a utility of synchrotron radiation, were applied for this experiment. As a result, the violet-blue absorption band (centered around 450-460 nm) as well as green absorption band (centered around 520 nm) were obviously decreased along the c-axis after heating, and XAS analysis indicated the increasing of the oxidation state of vanadium. This result was well supported by the chemical composition of samples. Consequently, vanadium was strongly suggested as the significant coloring agent in tanzanite after heat treatment.

GZ7 and GZ8 - Two Zircon Reference Materials for SIMS U-Pb Geochronology.

Here, we document a detailed characterisation of two zircon gemstones, GZ7 and GZ8. Both stones had the same mass at 19.2 carats (3.84 g) each; both came from placer deposits in the Ratnapura district, Sri Lanka. The U-Pb data are in both cases concordant within the uncertainties of decay constants and yield weighted mean 206Pb/238U ages (95% confidence uncertainty) of 530.26 Ma ± 0.05 Ma (GZ7) and 543.92 Ma ± 0.06 Ma (GZ8). Neither GZ7 nor GZ8 have been subjected to any gem enhancement by heating. Structure-related parameters correspond well with the calculated alpha doses of 1.48 × 1018 g-1 (GZ7) and 2.53 × 1018 g-1 (GZ8), respectively, and the (U-Th)/He ages of 438 Ma ± 3 Ma (2s) for GZ7 and 426 Ma ± 9 Ma (2s) for GZ8 are typical of unheated zircon from Sri Lanka. The mean U mass fractions are 680 µg g-1 (GZ7) and 1305 µg g-1 (GZ8). The two zircon samples are proposed as reference materials for SIMS (secondary ion mass spectrometry) U-Pb geochronology. In addition, GZ7 (Ti mass fractions 25.08 µg g-1 ± 0.18 µg g-1; 95% confidence uncertainty) may prove useful as reference material for Ti-in-zircon temperature estimates.