Voids Development in Metals: Numerical Modelling.

The article is a continuation of two previous review papers on the fracture mechanism of structural metals through the nucleation, growth and coalescence of voids. In the present paper, the literature on the numerical modelling of void nucleation and development has been reviewed. The scope of the work does not include porous material models and their numerical implementation. As part of the discussion on void initiation, nucleation around second phase particles and nucleation as an effect of the discontinuity of the crystal structure were discussed separately. The basic void cell models, finite element method (FEM) models of periodically distributed particles/voids and models based on the results of the observations of the actual microstructure of materials have been characterised. Basic issues related to the application of the cohesive approach in void nucleation modelling have been considered. A separate issue is the characteristics of atomistic simulations and peridynamic modelling, which have been developed in recent years. Numerical approaches to modelling the growth and coalescence of voids are described, with particular emphasis on the influence of the stress state and strain localisation. Basic conclusions from the simulation are presented, pointing to the contribution of FEM modelling to the understanding of microstructural phenomena leading to ductile fracture.

Void-Induced Ductile Fracture of Metals: Experimental Observations.

The paper presents a literature review on the development of microvoids in metals, leading to ductile fracture associated with plastic deformation, without taking into account the cleavage mechanism. Particular emphasis was placed on the results of observations and experimental studies of the characteristics of the phenomenon itself, without in-depth analysis in the field of widely used FEM modelling. The mechanism of void development as a fracture mechanism is presented. Observations of the nucleation of voids in metals from the turn of the 1950s and 1960s to the present day were described. The nucleation mechanisms related to the defects of the crystal lattice as well as those resulting from the presence of second-phase particles were characterised. Observations of the growth and coalescence of voids were presented, along with the basic models of both phenomena. The modern research methods used to analyse changes in the microstructure of the material during plastic deformation are discussed. In summary, it was indicated that understanding the microstructural phenomena occurring in deformed material enables the engineering of the modelling of plastic fracture in metals.

Some Microstructural Aspects of Ductile Fracture of Metals.

The paper discusses the basic issues of the local approach to ductile fracture of structural metals, with particular emphasis on the failure due to microvoid development. The mechanisms of nucleation of voids around inclusions and precipitates are characterized. The criteria for the nucleation of voids resulting from cracking of the existing particles or their separation from the material matrix are presented. Selected results of experimental studies and Finite Element Method (FEM) simulations on nucleation of voids are discussed. The analytical and numerical models of growth and coalescence of voids are described, indicating the effect of the stress state components on the morphology of voids and the course of the cracking on a microscopic scale.