RESUMO
OBJECTIVE: To compare the effect of different surface processes on bond strength and microscopic structure using a scanning electron microscope (SEM) and an energy distribution spectrum (EDS) at the bonding interface between zirconia framework and veneering ceramic. METHODS: WIELAND zirconia core material was cut into 33 rectangular specimens and fired on into rectangular specimens (10 mm×5 mm×5 mm). The specimens were randomly divided into three groups (n=â©11). The sandblasting group was sandblasted before firing. The sandblasting and liner coverage group was sandblasted before firing and then sintered with liner coverage after firing. The control group was not processed. All the veneering ceramics (5 mm×â©5 mm×5 mm) were fired on into the zirconia substructure by slip-casting technique. One bilayered specimen in each group was prepared for SEM and EDS to examine the bonding conditions. The other specimens were measured for shear force using an electronic universal dynamometer. The data obtained were analyzed by using the statistical software SPSS 17.0. RESULTS: The values of the shear bond strength test were (13.80±1.54) MPa for the control group, (18.06±0.59) MPa for the sandblasting group, and (21.04±1.23) MPa for the sandblasting and liner coverage group. Significant differences existed among the three groups (P<0.01). CONCLUSIONS: Abrasion before firing significantly increases the shear bond strength of zirconia to veneering porcelain. The use of porcelain combined with liner increases the shear bond strength.