Annealing effects on the magnetic and magnetotransport properties of iron oxide nanoparticles self-assemblies.

In magnetic tunnel junctions based on iron oxide nanoparticles the disorder and the oxidation state of the surface spin as well as the nanoparticles functionalization play a crucial role in the magnetotransport properties. In this work, we report a systematic study of the effects of vacuum annealing on the structural, magnetic and transport properties of self-assembled ∼10 nm Fe3O4nanoparticles. The high temperature treatment (from 573 to 873 K) decomposes the organic coating into amorphous carbon, reducing the electrical resistivity of the assemblies by 4 orders of magnitude. At the same time, the 3.Fe2+/(Fe3++Fe2+) ratio is reduced from 1.11 to 0.13 when the annealing temperature of the sample increases from 573 to 873 K, indicating an important surface oxidation. Although the 2 nm physical gap remains unchanged with the thermal treatment, a monotonous decrease of tunnel barrier width was obtained from the electron transport measurements when the annealing temperature increases, indicating an increment in the number of defects and hot-spots in the gap between the nanoparticles. This is reflected in the reduction of the spin dependent tunneling, which reduces the interparticle magnetoresistance. This work shows new insights about influence of the nanoparticle interfacial composition, as well their the spatial arrangement, on the tunnel transport of self-assemblies, and evidence the importance of optimizing the nanostructure fabrication for increasing the tunneling current without degrading the spin polarized current.

Reactive Oxygen Species in Emulated Martian Conditions and Their Effect on the Viability of the Unicellular Alga Scenedesmus dimorphus.

Formation of oxygen-based free radicals from photochemical decomposition of hydrogen peroxide (H2O2) on Mars may be a key factor in the potential survival of terrestrial-like organisms on the red planet. Martian conditions that generate reactive oxygen species involve the decomposition of H2O2 at temperatures of around 278 K under relatively high doses of C-band ultraviolet radiation (UVC). This process is further amplified by the presence of iron oxides and perchlorates. Photosynthetic organisms exhibit a number of evolutionary traits that allow them to withstand both oxidative stress and UVC radiation. Here, we examine the effect of free radicals produced by the decomposition of H2O2 under emulated martian conditions on the viability of Scenedesmus dimorphus, a unicellular alga that is resistant to UVC radiation and varying levels of perchlorate and H2O2, both of which are present on Mars. Identification and quantification of free radicals formed under these conditions were performed with Electron Paramagnetic Resonance spectroscopy. These results were correlated with the viability of S. dimorphus, and the formation of oxygen-based free radicals and survival of the alga were found to be strongly dependent on the amount of H2O2 available. For H2O2 amounts close to those present in the rarefied martian environment, the products of these catalytic reactions did not have a significant effect on the algal population growth curve.

Adjusting the Néel relaxation time of Fe3O4/Zn x Co1-x Fe2O4 core/shell nanoparticles for optimal heat generation in magnetic hyperthermia.

In this work it is shown a precise way to optimize the heat generation in high viscosity magnetic colloids, by adjusting the Néel relaxation time in core/shell bimagnetic nanoparticles, for magnetic fluid hyperthermia (MFH) applications. To pursue this goal, Fe3O4/Zn x Co1-x Fe2O4 core/shell nanoparticles were synthesized with 8.5 nm mean core diameter, encapsulated in a shell of ∼1.1 nm of thickness, where the Zn atomic ratio (Zn/(Zn + Co) at%) changes from 33 to 68 at%. The magnetic measurements are consistent with a rigid interface coupling between the core and shell phases, where the effective magnetic anisotropy systematically decreases when the Zn concentration increases, without a significant change of the saturation magnetization. Experiments of MFH of 0.1 wt% of these particles dispersed in water, in Dulbecco modified Eagles minimal essential medium, and a high viscosity butter oil, result in a large specific loss power (SLP), up to 150 W g-1, when the experiments are performed at 571 kHz and 200 Oe. The SLP was optimized adjusting the shell composition, showing a maximum for intermediate Zn concentration. This study shows a way to maximize the heat generation in viscous media like cytosol, for those biomedical applications that require smaller particle sizes.

Effects of biological buffer solutions on the peroxidase-like catalytic activity of Fe3O4 nanoparticles.

Iron oxide nanoparticles (IONPs) are frequently used in biomedical applications due to their magnetic properties and putative chemical stability. Nevertheless, their well-known ability to mimic some features of the peroxidase enzyme activity under specific conditions of pH and temperature could lead to the formation of potentially harmful free radical species. In addition to the intrinsic enzyme-like activity of IONPs, the buffer solution is an important external factor that can alter dramatically the IONP activity because the buffer species can interact with the surface of the particles. In our study, IONP activity was evaluated in different buffering solutions under different experimental conditions and predominant free radical species were measured by electron paramagnetic resonance using the spin-trap 5,5-dimethyl-1-pyrroline N-oxide (DMPO). The formation kinetics of the reactive oxygen species were studied by UV-visible spectroscopy with TMB and DAB peroxidase substrates. We found that the highest catalytic oxidation of peroxidase substrates and free radical generation were achieved in acetate buffer, while phosphate buffer inhibited the peroxidase-like activity of IONPs in a concentration dependent manner. When emulating the physiological conditions, a lower catalytic activity was observed at pH 7.4 when compared to that at pH 5.0. Also, in phosphate buffered saline (PBS), we observed an enhancement in the peroxidase substrate oxidation rate that was not accompanied by an increase in DMPO/adduct formation which could be related to a non-specific oxidation catalyzed by the chloride ion. Similar observations were found after the addition of a bicarbonate to HEPES buffer. TMB oxidation did not occur when the reaction was conducted with free iron ions from metal salts with the same concentration of the IONPs (0.33 Fe2+ and 0.66 Fe3+). However, we observed even higher catalytic activities than those when doubling the IONP concentration when they are combined with the free iron salts. These results indicate that biological buffering solutions need to be carefully considered when evaluating IONP catalytic activity and their potential toxicological effects since under physiological conditions of pH, salinity and buffering species, the peroxidase-like activity of IONPs is dramatically reduced.

Controlling the dominant magnetic relaxation mechanisms for magnetic hyperthermia in bimagnetic core-shell nanoparticles.

We report a simple and effective way to control the heat generation of a magnetic colloid under alternate magnetic fields by changing the shell composition of bimagnetic core-shell Fe3O4/ZnxCo1-xFe2O4 nanoparticles. The core-shell structure constitutes a magnetically-coupled biphase system, with an effective anisotropy that can be tuned by the substitution of Co2+ by Zn2+ ions in the shell. Magnetic hyperthermia experiments of nanoparticles dispersed in hexane and butter oil showed that the magnetic relaxation is dominated by Brown relaxation mechanism in samples with higher anisotropy (i.e., larger concentration of Co within the shell) yielding high specific power absorption values in low viscosity media as hexane. Increasing the Zn concentration of the shell, diminishes the magnetic anisotropy, which results in a change to a Néel relaxation that dominates the process when the nanoparticles are dispersed in a high-viscosity medium. We demonstrate that tuning the Zn contents at the shell of these exchange-coupled core/shell nanoparticles provides a way to control the magnetic anisotropy without loss of saturation magnetization. This ability is an essential prerequisite for most biomedical applications, where high viscosities and capturing mechanisms are present.

Tuning the coercivity and exchange bias by controlling the interface coupling in bimagnetic core/shell nanoparticles.

In order to explore an alternative strategy to design exchange-biased magnetic nanostructures, bimagnetic core/shell nanoparticles have been fabricated by a thermal decomposition method and systematically studied as a function of the interface exchange coupling. The nanoparticles are constituted by a ∼3 nm antiferromagnetic (AFM) CoO core encapsulated in a ∼4 nm-thick Co1-xZnxFe2O4 (x = 0-1) ferrimagnetic (FiM) shell. The system presents an enhancement of the coercivity (HC) as compared to its FiM single-phase counterpart and exchange bias fields (HEB). While HC decreases monotonically with the Zn concentration from ∼21.5 kOe for x = 0, to ∼7.1 kOe for x = 1, HEB exhibits a non-monotonous behavior being maximum, HEB ∼ 1.4 kOe, for intermediate concentrations. We found that the relationship between the AFM anisotropy energy and the exchange coupling energy can be tuned by replacing Co2+ with Zn2+ ions in the shell. As a consequence, the magnetization reversal mechanism of the system is changed from an AFM/FiM rigid-coupling regime to an exchange-biased regime, providing a new approach to tune the magnetic properties and to design novel hybrid nanostructures.

Temperature evolution of the effective magnetic anisotropy in the MnCr2O4 spinel.

In this work, we present a study of the low temperature magnetic phases of polycrystalline MnCr2O4 spinel through dc magnetization and ferromagnetic resonance spectroscopy (FMR). Through these experiments, we determined the main characteristic temperatures: T(C) ∼ 41 K and T(H) ∼ 18 K corresponding, respectively, to the ferrimagnetic order and to the low temperature helicoidal transitions. The temperature evolution of the system is described by a phenomenological approach that considers the different terms that contribute to the free energy density. Below the Curie temperature, the FMR spectra were modeled by a cubic magnetocrystalline anisotropy to the second order, with K1 and K2 anisotropy constants that define the easy magnetization axis along the <1 1 0> direction. At lower temperatures, the formation of a helicoidal phase was considered by including uniaxial anisotropy axis along the [11¯0] propagation direction of the spiral arrange, with a Ku anisotropy constant. The values obtained from the fittings at 5 K are K1 = -2.3 × 10(4) erg cm(-3), K2 = 6.4 × 10(4) erg cm(-3) and Ku = 7.5 × 10(4) erg cm(-3).

Size effects in bimagnetic CoO/CoFe2O4 core/shell nanoparticles.

The control of the size of bimagnetic nanoparticles represents an important step toward the study of fundamental properties and the design of new nanostructured magnetic materials. We report the synthesis and the structural and magnetic characterization of bimagnetic CoO/CoFe2O4 core/shell nanoparticles. The material was fabricated by a seed-mediated growth high-temperature decomposition method with sizes in the range of 5-11 nm. We show that the core/shell morphology favours the crystallinity of the shell phase, and the reduction of the particle size leads to a remarkable increase of the magnetic hardening. When the size is reduced, the coercive field at 5 K increases from 21.5 kOe to 30.8 kOe, while the blocking temperature decreases from 388 K to 167 K. The size effects on the magnetic behaviour are described through a phenomenological model for strongly ferri-/antiferromagnetic coupled phases.