RESUMO
A fuel cell, an energy transducer, can convert chemical energy into electrical energy. In this work, graphite felt (GF) loaded with polypyrrole (PPy) and carboxylic carbon nanotubes (CNTs-COOH) was used as a cathode (GF/PPy/CNTs-COOH) in a double-chamber nonbiofuel cell (D-nBFC) to remove Cr(VI) efficiently. Therein, Na2S2O3 in an alkaline solution and Cr(VI) in a strongly acidic solution were employed as anode and cathode solutions, respectively. An agar salt bridge, consisting of saturated KCl solution, was used to transport ions between the anode and cathode. This system suggested that the removal efficiency of Cr(VI) could reach 99.6%. The maximum current, power, and power density could achieve 136.8 µA, 18.7 µW, and 20.8 mW/m2 at 90 min, respectively. Additionally, GF/PPy/CNTs-COOH also had good electrocatalytic stability and reusability after four cycles, which played an important role in the development of the D-nBFC system. Therefore, this study provides an environmentally friendly and efficient method to remove Cr(VI) and generate electricity simultaneously.
RESUMO
Electrohydrodynamic jet printing (EJP) is a developing additive manufacture technology that enables the fabrication of fine scaffolds directly from polymer solutions or melt. Timely solidification of the polymer jet is the key factor for the success of EJP process. In conventional solution-based EJP methods, it is usually achieved by rapid solvent evaporation and producing a scaffold with smooth filaments. In current study, by combining solution-based EJP with a cryogenic workbench, a cryogenic electrohydrodynamic jet printing (CEJP) system was developed, in which the polymer jet was frozen and solidified quickly at the freezing temperature rather than solvent evaporation. The feasibility and versatility of the CEJP system were verified by successful printing of scaffolds with different hole shapes and pore sizes. Meanwhile, the resulting scaffolds not only had a resolution in the range of 50-80 µm but also possessed oriented "ridges" and "valleys" on surface of the filaments, which was conductive to cell orientation. Therefore, this work provides a novel method to print fine scaffolds with extra surface topography.