RESUMO
Parallel striations made of silver nanowires were formed through the Marangoni instability induced during spin casting of poly(2-vinyl pyridine)/silver nanowire/chloroform solutions. The striation patterns of the silver nanowires resembled those obtained from spin casting of the corresponding neat polymer solutions, indicating essentially the same driving mechanism (i.e., the Marangoni instability). The silver nanowires were found to concentrate in the valleys of the striation pattern to balance the nonuniform surface tension distribution in the polymer thin film. The resulting nanowire striation patterns were found to depend on polymer concentration, rotational speed, and nanowire loading. Interestingly, this nanowire striation phenomenon was found to be independent of the substrate characteristics, hydrophobic or hydrophilic.
RESUMO
Patterns of parallel strips, consisting of alternating polystyrene (PS) and poly(vinyl pyrrolidone) (PVP) regions, were observed in thin films spin cast from a PS/PVP/chloroform solution on unpatterned substrates. The formation of anisotropic patterns, manifested not only in thickness variation but also in composition variation, was found to be driven by Marangoni instability, with the PS and PVP streams flowing toward the preferred regions as the phase separation induced by solvent evaporation proceeded. The initial viscosity of the polymer solution and the thickness of the spin-cast films were lumped into one single parameter to study the phase morphology development at various initial polymer solution concentrations. Interestingly, the ratio of the square of the film thickness to the viscosity, a parameter loosely related to the Marangoni number, was found to reach a maximum value at the concentration where the strip patterns were most well-developed.