Determining the Gibbs Energy Contributions of Ion and Electron Transfer for Proton Insertion in ϵ-MnO2.

Electrochemically active ϵ-MnO2 and ɣ-MnO2 as tunnel-type host-guest structures have been extensively studied by crystallography and electrochemical techniques for application in battery cathode materials. However, the Gibbs energies of the underlying ion and electron transfer processes across the electrode interfaces have not yet been determined. Here we report for the first time these data for ϵ-MnO2 . This was possible by measuring the mid-peak potentials in cyclic voltammetry and the open-circuit potentials under electrochemically reversible conditions.

Seaweed and Dendritic Growth in Unsaturated Fatty Acid Monolayers.

The lateral movement in lipid membranes depends on their diffusion constant within the membrane. However, when the flux of the subphase is high, the convective flow beneath the membrane also influences lipid movement. Lipid monolayers of an unsaturated fatty acid at the water-air interface serve as model membranes. The formation of domains in the liquid/condensed coexistence region is investigated. The dimension of the domains is fractal, and they grow with a constant growth velocity. Increasing the compression speed of the monolayer induces a transition from seaweed growth to dendritic growth. Seaweed domains have broad tips and wide and variable side branch spacing. In contrast, dendritic domains have a higher fractal dimension, narrower tips, and small, well-defined side branch spacing. Additionally, the growth velocity is markedly larger for dendritic than seaweed growth. The domains' growth velocity increases and the tip radius decreases with increasing supersaturation in the liquid/condensed coexistence region. Implications for membranes are discussed.

Surface Stoichiometry and Depth Profile of Tix-CuyNz Thin Films Deposited by Magnetron Sputtering.

We report the surface stoichiometry of Tix-CuyNz thin film as a function of film depth. Films are deposited by high power impulse (HiPIMS) and DC magnetron sputtering (DCMS). The composition of Ti, Cu, and N in the deposited film is investigated by X-ray photoelectron spectroscopy (XPS). At a larger depth, the relative composition of Cu and Ti in the film is increased compared to the surface. The amount of adventitious carbon which is present on the film surface strongly decreases with film depth. Deposited films also contain a significant amount of oxygen whose origin is not fully clear. Grazing incidence X-ray diffraction (GIXD) shows a Cu3N phase on the surface, while transmission electron microscopy (TEM) indicates a polycrystalline structure and the presence of a Ti3CuN phase.

Nonaqueous atomic layer deposition of aluminum phosphate.

Aluminum phosphate was deposited onto bundles of carbon fibers and flat glassy carbon substrates using atomic layer deposition by exposing them to alternating pulses of trimethylaluminum and triethylphosphate vapors. Energy dispersive X-ray spectroscopy (EDXS) and solid state nuclear magnetic resonance (SS-NMR) spectra confirmed that the coating comprises aluminum phosphate (orthophosphate as well as other stoichiometries). Scanning electron microscopic (SEM) images revealed that the coatings are uniform and conformal. After coating, the fibers are still separated from each other like the uncoated fibers. Thermogravimetric analysis (TGA) indicates an improvement of oxidation resistance of the coated fibers compared to uncoated fibers.

Structure, insertion electrochemistry, and magnetic properties of a new type of substitutional solid solutions of copper, nickel, and iron hexacyanoferrates/hexacyanocobaltates.

Substitutional solid solutions of metal hexacyanometalates in which low-spin iron(III) and cobalt(III) ions populate the carbon-coordinated sites were synthesized and studied by powder diffraction including Rietveld refinement, cyclic voltammetry of immobilized microparticles, diffuse reflection vis-spectrometry, and magnetization techniques. The continuous solid solution series of potassium copper(II), potassium nickel(II), and iron(III) [(hexacyanoferrate(III))(1-x)(hexacyanocobaltate(III))(x)] show that the substitution of low-spin iron(III) by cobalt(III) in the hexacyanometalate units more strongly affects the formal potentials of the nitrogen-coordinated copper(II) and high-spin iron(III) ions than those of the remaining low-spin iron(III) ions. In the case of copper(II) and iron(III) [(hexacyanoferrate(III))(1-x)(hexacyanocobaltate(III))(x)] the peak currents decrease much more than can be explained by stoichiometry, indicating that the charge propagation is slowed by the substitution of low-spin iron(III) by cobalt(III). The Rietveld refinement of all compounds confirmed the structure initially proposed by Keggin for Prussian blue and contradicts the structure described later by Ludi. The dependencies of lattice parameters on composition exhibit in all series of solid solutions studied similar, although small, deviations from ideality, which correlate with the electrochemical behavior. Finally, a series of solid solutions of the composition KNi(0.5)(II)Cu(0.5)(II)[Fe(III)(CN)(6)](1-x)[Co(III)(CN)(6)](x), where both the nitrogen- and carbon-coordinated metal ions are mixed populated and were synthesized and characterized. These are the first examples of solid solutions of metal hexacyanometalates with four different metal ions, where both the nitrogen- and the carbon-coordinated sites possess a mixed population.