Meeting the Needs for Released Nanomaterials Required for Further Testing-The SUN Approach.

The analysis of the potential risks of engineered nanomaterials (ENM) has so far been almost exclusively focused on the pristine, as-produced particles. However, when considering a life-cycle perspective, it is clear that ENM released from genuine products during manufacturing, use, and disposal is far more relevant. Research on the release of materials from nanoproducts is growing and the next necessary step is to investigate the behavior and effects of these released materials in the environment and on humans. Therefore, sufficient amounts of released materials need to be available for further testing. In addition, ENM-free reference materials are needed since many processes not only release ENM but also nanosized fragments from the ENM-containing matrix that may interfere with further tests. The SUN consortium (Project on "Sustainable Nanotechnologies", EU seventh Framework funding) uses methods to characterize and quantify nanomaterials released from composite samples that are exposed to environmental stressors. Here we describe an approach to provide materials in hundreds of gram quantities mimicking actual released materials from coatings and polymer nanocomposites by producing what is called "fragmented products" (FP). These FP can further be exposed to environmental conditions (e.g., humidity, light) to produce "weathered fragmented products" (WFP) or can be subjected to a further size fractionation to isolate "sieved fragmented products" (SFP) that are representative for inhalation studies. In this perspective we describe the approach, and the used methods to obtain released materials in amounts large enough to be suitable for further fate and (eco)toxicity testing. We present a case study (nanoparticulate organic pigment in polypropylene) to show exemplarily the procedures used to produce the FP. We present some characterization data of the FP and discuss critically the further potential and the usefulness of the approach we developed.

Size matters--The phototoxicity of TiO2 nanomaterials.

Under solar radiation several titanium dioxide nanoparticles (nano-TiO2) are known to be phototoxic for daphnids. We investigated the influence of primary particle size (10, 25, and 220 nm) and ionic strength (IS) of the test medium on the acute phototoxicity of anatase TiO2 particles to Daphnia magna. The intermediate sized particles (25 nm) showed the highest phototoxicity followed by the 10 nm and 220 nm sized particles (median effective concentrations (EC50): 0.53, 1.28, 3.88 mg/L). Photoactivity was specified by differentiating free OH radicals (therephthalic acid method) and on the other hand surface adsorbed, as well as free OH, electron holes, and O2(-) (electron paramagnetic resonance spectroscopy, EPR). We show that the formation of free OH radicals increased with a decrease in primary particle size (terephthalic acid method), whereas the total measured ROS content was highest at an intermediate particle size of 25 nm, which consequently revealed the highest photoxicity. The photoactivities of the 10 and 220 nm particles as measured by EPR were comparable. We suggest that phototoxicity depends additionally on the particle-daphnia interaction area, which explains the higher photoxicity of the 10 nm particles compared to the 220 nm particles. Thus, phototoxicity is a function of the generation of different ROS and the particle-daphnia interaction area, both depending on particle size. Phototoxicity of the 10 nm and 25 nm sized nanoparticles decreased as IS of the test medium increased (EC50: 2.9 and 1.1 mg/L). In conformity with the Derjaguin-Landau-Verwey-Overbeek (DLVO) theory we suggest that the precipitation of nano-TiO2 was more pronounced in high than in low IS medium, causing a lower phototoxicity. In summary, primary particle size and IS of the medium were identified as factors influencing phototoxicity of anatase nano-TiO2 to D. magna.