2D/1D V2O5 Nanoplates Anchored Carbon Nanofibers as Efficient Separator Interlayer for Highly Stable Lithium-Sulfur Battery.

Quick capacity loss due to the polysulfide shuttle effects is a critical challenge for high-performance lithium-sulfur (Li-S) batteries. Herein, a novel 2D/1D V2O5 nanoplates anchored carbon nanofiber (V-CF) interlayer coated on standard polypropylene (PP) separator is constructed, and a stabilization mechanism derived from a quasi-confined cushion space (QCCS) that can flexibly accommodate the polysulfide utilization is demonstrated. The incorporation of the V-CF interlayer ensures stable electron and ion pathway, and significantly enhanced long-term cycling performances are obtained. A Li-S battery assembled with the V-CF membrane exhibited a high initial capacity of 1140.8 mAh·g-1 and a reversed capacitance of 1110.2 mAh·g-1 after 100 cycles at 0.2 C. A high reversible capacity of 887.2 mAh·g-1 is also maintained after 500 cycles at 1 C, reaching an ultra-low decay rate of 0.0093% per cycle. The excellent electrochemical properties, especially the long-term cycling stability, can offer a promising designer protocol for developing highly stable Li-S batteries by introducing well-designed fine architectures to the separator.

Linear-Polyethyleneimine-Templated Synthesis of N-Doped Carbon Nanonet Flakes for High-performance Supercapacitor Electrodes.

Novel N-doped carbon nanonet flakes (NCNFs), consisting of three-dimensional interconnected carbon nanotube and penetrable mesopore channels were synthesized in the assistance of a hybrid catalytic template of silica-coated-linear polyethyleneimine (PEI). Resorcinol-formaldehyde resin and melamine were used as precursors for carbon and nitrogen, respectively, which were spontaneously formed on the silica-coated-PEI template and then annealed at 700 °C in a N2 atmosphere to be transformed into the hierarchical 3D N-doped carbon nanonetworks. The obtained NCNFs possess high surface area (946 m2 g-1), uniform pore size (2-5 nm), and excellent electron and ion conductivity, which were quite beneficial for electrochemical double-layered supercapacitors (EDLSs). The supercapacitor synthesized from NCNFs electrodes exhibited both extremely high capacitance (up to 613 F g-1 at 1 A g-1) and excellent long-term capacitance retention performance (96% capacitive retention after 20,000 cycles), which established the current processing among the most competitive strategies for the synthesis of high performance supercapacitors.