RESUMO
Zinc (Zn) alloys have attracted much attention for biomedical applications due to their biodegradability, biocompatibility, and biological functionalities. Zn alloy foams have high potential to be used as regenerative medical implants by virtue of their porous structure, which allows new bone tissue ingrowth, their low elastic modulus approximating that of natural bone, and their biodegradation, which eliminates the need for follow-up surgery to remove the implants after bone tissue healing. In this context, a biodegradable Zn-Cu foam was fabricated by electrochemical deposition on a foamed Cu template and given a subsequent diffusion heat treatment. The microstructure, mechanical properties, degradation behavior, toxicity, hemolysis percentages, and antibacterial effects of the Zn-Cu foams were assessed for biomedical applications. The Zn-Cu foams exhibited a yield strength of ~12.1 MPa, a plateau strength of 16.8 MPa, and a strain over 50% under compression tests. The corrosion rate of the Zn-Cu foams measured by electrochemical polarization testing was 0.18 mm/y. The Zn-Cu foams showed good blood compatibility with a hemolysis percentage of less than 5%. Cytotoxicity assessment indicated that a 100% concentration of the Zn-Cu foam extract showed clear cytotoxicity against MC3T3-E1 osteoblast cells, but a 12.5% concentration of the extract showed > 90% cell viability. Moreover, the Zn-Cu foams showed good antibacterial effects. STATEMENT OF SIGNIFICANCE: This work reportsa biodegradable Zn-Cu foam with high mechanical strength and ductility, suitable degradation rate, good antibacterial capacity, and good hemolysis property and biocompatibility. The Zn-Cu foam exhibited a yield strength of ~12.1 MPa, a plateau strength of 16.8 MPa, and a strain over 50% under compression tests. The corrosion rate of the Zn-Cu foam measured by electrochemical polarization testing was 0.18 mm/y in Hanks' Solutions. The Zn-Cu foam showed good blood compatibility with a hemolysis percentage of less than 5%. Cytotoxicity assessment indicated that a 12.5% concentration of the foam extract showed > 90% cell viability. Moreover, the Zn-Cu foam showed good antibacterial effects against S. aureus.