The application of CFRP bar and seawater sea-sand concrete (SSSC) in construction can overcome the shortcomings in conventional reinforced concrete, such as corrosion induced by carbonation and chloride ingress. In this study, the bond-slip behavior between an SSSC cube and CFRP bar has been investigated, and different CFRP bar surface shapes have been considered. A total of 27 specimens (9 groups) were fabricated for a pull-out test, where three types of CFRP bar with different surface shapes were used: smooth regular bars, double-wrapped bars and ribbed bars. Bond strength, bond-slip curve, and failure mode have been presented and discussed. FE models have been constructed and validated by experimental results. The effect of concrete compressive strength and relative area of ribs on bond strength has been studied through numerical simulations. It is found that the bond strength increased with concrete compressive strength, and the ribbed bar had significantly higher bond strength than the smooth regular bar. Pull-out failure was observed when the cover-depth-to-bar-diameter ratio was no less than 4 and, otherwise, splitting failure occurred. In addition, a simple formula has been proposed to approximately evaluate the bond strength between an SSSC cube and CFRP bar and validated by experimental results, and analytical expressions for different bond-slip curves have also been developed.
RESUMO
The hanger is one of the important components for through and half-through arch bridges. Conventional steel hangers are vulnerable to corrosion due to corrosive environments. Therefore, a new type of bridge hangers consisting of Carbon Fiber-Reinforced Polymer (CFRP) straps was developed recently. The CFRP straps are self-anchored, which is formed by layers-winding, and they have great advantages in corrosive environments such as high resistance to corrosion. In this study, the fatigue and fracture behavior of CFRP straps has been experimentally investigated. Firstly, the tensile testing of four CFRP strap specimens was conducted to investigate the static fracture behavior of CFRP straps, and three stages were observed, including delamination, cracking, and brittle rupture. Then, a fatigue test of thirty-nine specimens (four groups) was carried out to study the fatigue behavior of CFRP straps, where two types of pins, titanium alloy pin and CFRP pin, and two loading frequencies, 10 Hz and 15 Hz, were used. The number of cycles to failure, displacement, fatigue failure strain, outside surface temperature at the vertex of specimen, and scanning electron microscope (SEM) photographs were recorded and analyzed to investigate the fatigue behavior of CFRP straps. The experiment results show that the temperature development at the vertex of the CFRP strap varies obviously if different pins are used due to the different friction coefficients. In addition, the fatigue life of CFRP straps decreases significantly with the increase in loading rate for the titanium pin, while it only reduces slightly with the increase in loading rate for the CFRP pin.