RESUMO
This experimental study aims to examine the partial discharge (PD) properties of palm oil and coconut oil (CO) based aluminum oxide (Al2O3) nanofluids with and without surfactants. The type of surfactant used in this study was sodium dodecyl sulfate (SDS). The volume concentrations range of Al2O3 dispersed in oil samples was varied from 0.001% to 0.05%. The ratio of surfactants to nanoparticles was set to 1:2. In total, two different types of refined, bleached and deodorized palm oil (RBDPO) and one type of CO were measured for PD. Mineral oil (MO) was also examined for comparison purpose. PDIV measurements for all samples were carried out based on rising voltage method whereby a needle-sphere electrode configuration with a gap distance of 50 mm was chosen in this study. Al2O3 improves the PDIVs of RBDPO, CO and MO whereby the highest improvements of PDIVs are 34%, 39.3% and 27%. The PD amplitude and repetition rate of RBDPO improve by 38% and 81% while for CO, it can increase up to 65% and 80% respectively. The improvement of PD amplitude and repetition rate for MO are 18% and 95%, regardless with and without SDS. Without SDS, the presence of Al2O3 could cause 26%, 75% and 65% reductions of the average emission of light signals for RBDPOA, RBDPOB and CO with the improvement of PD characteristics but both events do not correlate at the same volume concentration of Al2O3. On the other hand, the average emission of light signal levels of the oils increases with the introduction of SDS. The emission of light signal in MO does not correlate with the PD characteristics improvement either with or without SDS.
RESUMO
In this paper, the effect of different types of surfactants on the lightning breakdown voltages of palm oil (PO) and coconut oil (CO) based aluminium oxide (Al2O3) nanofluids is investigated. Three different types of surfactants were used in this study known as cationic (cetyl trimethyl ammonium bromide (CTAB)), anionic (sodium dodecyl sulfate (SDS)) and non-ionic (oleic acid (OA)). The volume percentage concentrations of Al2O3 dispersed into PO and CO were varied from 0.001% to 0.05%. The ratio of surfactant to the nanoparticles was set to 50% from the volume concentration of nanoparticles which equivalent to 1:2. In total, two types of refined, bleached and deodorized palm oil (RBDPO) and one type of CO were examined for lightning breakdown voltage. The test was carried out based on needle-sphere electrodes configuration with 25 mm gap distance. The presence of Al2O3 improves both positive and negative lightning breakdown voltages of RBDPO and CO. Under the positive and negative polarities, the CTAB does provide further improvements on the lightning breakdown voltages of RBDPOA (1st type of samples) and CO at most of the volume of concentration of Al2O3. SDS and OA could also further improve the lightning breakdown voltage of CO at certain volume concentration of Al2O3. On the other hand, the lightning breakdown voltage of RBDPOB based Al2O3 nanofluid (2nd type of samples) does not further improve with the introduction of surfactants. At most of the volume concentration of Al2O3, the introduction of CTAB further increases the times to breakdown and decrease the average streamer velocities of RBDPOA under both polarities. The same finding is observed for CO under positive polarity with CTAB and SDS as well as under negative polarity in the presence of all surfactants. The streamer velocities and times to breakdown patterns of RBDPOB based Al2O3 nanofluid are inconsistent in the presence of all surfactants. It is found that RBDPO and CO based Al2O3 nanofluids have second mode of streamer whereby the streamer velocities are from 1 km s-1 to 1.63 km s-1 regardless with or without surfactants.
RESUMO
This paper presents a sealed ageing study of palm oil (PO) and coconut oil (CO) in the presence of insulation paper. The type of PO under study is refined, bleached, and deodorized palm oil (RBDPO) olein. Three different variations of RBDPO and one sample of CO are aged at temperatures of 90 °C, 110 °C, and 130 °C. The properties of RBDPO and CO as well as paper under ageing are then analysed through dielectric and physicochemical measurements. It is found that the effect of ageing is not significant on the alternating current (AC) breakdown voltages and relative permittivities of RBDPO and CO. There is a slight increment trend of the resistivity for CO, while for all of the RBDPO, the resistivity slightly decreases as the ageing progresses. Only CO shows an apparent reduction of the dielectric dissipation factor. Throughout the ageing time, the acidities of all of the RBDPO and CO remain at low level, while the moisture in oils decreases. The tensile index (TI) of the papers for all of the RBDPO and CO retain more than 50% of the TI. A significant increment of the paper ageing rates of all of the RBDPO and CO is observed at an ageing temperature of 130 °C.
RESUMO
BACKGROUND: The transesterification of high oleic palm oil methyl ester (HOPME) with neopentyl glycol (NPG) has been investigated. The present study revealed the application of low-pressure technology as a new synthesis method to produce NPG diesters. Single variable optimization and response surface methodology (RSM) were implemented to optimize the experimental conditions to achieve the maximum composition (wt%) of NPG diesters. OBJECTIVE: The main objective of this study was to optimize the production of NPG diesters and to characterize the optimized esters with typical chemical, physical and electrical properties to study its potential as insulating oil. METHODS: The transesterification reaction between HOPME and NPG was conducted in a 1L three-neck flask reactor at specified temperature, pressure, molar ratio and catalyst concentration. For the optimization, four factors have been studied and the diester product was characterized by using gas chromatography (GC) analysis. The synthesized esters were then characterized with typical properties of transformer oil such as flash point, pour point, viscosity and breakdown voltage and were compared with mineral insulating oil and commercial NPG dioleate. For formulation, different samples of NPG diesters with different concentration of pour point depressant were prepared and each sample was tested for its pour point measurement. RESULTS: The optimum conditions inferred from the analyses were: molar ratio of HOPME to NPG of 2:1.3, temperature = 182°C, pressure = 0.6 mbar and catalyst concentration of 1.2%. The synthesized NPG diesters showed very important improvement in fire safety compared to mineral oil with flash point of 300°C and 155°C, respectively. NPG diesters also exhibit a relatively good viscosity of 21 cSt. The most striking observation to emerge from the data comparison with NPG diester was the breakdown voltage, which was higher than mineral oil and definitely in conformance to the IEC 61099 limit at 67.5 kV. The formulation of synthesized NPD diesters with VISCOPLEX® pour point depressant has successfully increased the pour point of NPG diester from -14°C to -48°C. CONCLUSION: The reaction time for the transesterification of HOPME with NPG to produce NPG diester was successfully reduced to 1 hour from the 14 hours required in the earlier synthesis method. The main highlight of this study was the excess reactant which is no longer methyl ester but the alcohol (NPG). The optimum reaction conditions for the synthesis were molar ratio of 2:1.13 for NPG:HOPME, 182°C, 0.6 mbar and catalyst concentration of 1.2 wt%. The maximum NPG diester yield of 87 wt% was consistent with the predicted yield of 87.7 wt% obtained from RSM. The synthesized diester exhibited better insulating properties than the commercial products especially with regards to the breakdown voltage, flash point and moisture content.