RESUMO
Acrylonitrile wastewater was an organic wastewater with strong toxicity and poor biodegradability. Therefore, electro-catalytic technology became a promising acrylonitrile wastewater treatment technology because of no secondary pollution, wide application range and low water quality requirements. The optimal Mn-Sn modified Ru-Ir electrode material was synthesized by thermal method and applied in electro-catalytic treatment of acrylonitrile wastewater. The electrode materials were characterized by SEM, TEM, XRD, XPS and electrochemical characterization. SEM, TEM, XRD and XPS indicated that Mn and Sn were capable of incorporating and replacing the part of Ru or Ir and could alter the microstructure of Ru-Ir and the types of Mn and Sn oxides, raising the oxygen evolution potential (OEP) and voltampere charge. When the molar ratio of Mn-Sn was 1:1, OEP, voltampere charge and exchange current density could reach 1.303 V, 1.51 C/cm2 and 6.29×10-4 A/cm2, respectively. The co-doping of Mn-Sn had significant influence on the electrocatalytic performance of Ru-Ir electrode materials. The optimum synthesis conditions of Mn-Sn modified Ru-Ir electrode were as follows: the molar ratio of Mn-Sn was 1:1, calcination time was 4.0 hours, calcination temperature was 450â, and solvent was water. Under certain conditions, the removal rate of acrylonitrile with Mn-Sn modified Ru-Ir electrode was 100%. Mn-Sn modified Ru-Ir electrode had high oxygen evolution potential and good removal effect of acrylonitrile, which was higher than that of ruthenium iridium electrode and RuO2 electrode.
Assuntos
Acrilonitrila , Acrilonitrila/química , Águas Residuárias , Cloretos , Eletrodos , OxigênioRESUMO
In this paper, Pd-Sn modified Ru-Ir electrode was prepared by thermal oxidation method, and the effects of doping amount of Pd-Sn and synthesis conditions on Pd-Sn modified Ru-Ir electrode performance were studied. Linear sweep voltammetry(LSV), cyclic voltammetry(CV), and the Tafel curve were used to study the electrochemical performance of the Pd-Sn modified Ru-Ir electrode materials. The effects of the doping amount of Pd-Sn on the microstructure and valence states of Pd-Sn modified Ru-Ir electrode materials were investigated by SEM, TEM, XRD, and XPS. When the mass of Pd-Sn accounted for 1.5% of the total mass of the elements, the molar ratio of Ru-Ir was 2:1, and the molar ratio of Pd-Sn was 3:1; the LSV, CV, and the Tafel curves indicated that Pd-Sn modified Ru-Ir electrode had the lowest chlorine evolution potential (1.0640 V vs. SCE), the best CV curve coincidence, and the smallest corrosion current density (6.5 × 10-4 A/cm2), showing the best chlorine evolution performance, the best durability, and corrosion resistance; the characterization of SEM, TEM, XRD, and XPS showed that Pd-Sn was successfully doped into Ru-Ir electrode materials; the crystallinity of Pd-Sn modified Ru-Ir electrode was the highest, and the binding energy was the lowest, but the crystal form of Ru-Ir solid solution did not have changed. The optimal synthesis conditions of Pd-Sn modified Ru-Ir electrode material were as follows: Pd-Sn molar ratio was 3:1, calcination temperature was 500 â, calcination time was 4 h, and water was used as solvent. Pd-Sn modified Ru-Ir electrode can efficiently treat high chlorine ammonia-nitrogen wastewater, when the reaction volume was 200 mL, the initial concentration of NH3-N was 100 mg/L, the concentration of chloride ion was 5000 mg/L, the current was 0.75 A, and the reaction time was 40 min; the removal rate of ammonia nitrogen can reach 100%.Responsible editor: Weiming Zhang.