Development of a superconducting bulk magnet for NMR and MRI.

A superconducting bulk magnet composed of six vertically stacked annular single-domain c-axis-oriented Eu-Ba-Cu-O crystals was energized to 4.74 T using a conventional superconducting magnet for high-resolution NMR spectroscopy. Shim coils, gradient coils, and radio frequency coils for high resolution NMR and MRI were installed in the 23 mm-diameter room-temperature bore of the bulk magnet. A 6.9 ppm peak-to-peak homogeneous region suitable for MRI was achieved in the central cylindrical region (6.2 mm diameter, 9.1 mm length) of the bulk magnet by using a single layer shim coil. A 21 Hz spectral resolution that can be used for high resolution NMR spectroscopy was obtained in the central cylindrical region (1.3 mm diameter, 4 mm length) of the bulk magnet by using a multichannel shim coil. A clear 3D MR image dataset of a chemically fixed mouse fetus with (50 µm)(3) voxel resolution was obtained in 5.5 h. We therefore concluded that the cryogen-free superconducting bulk magnet developed in this study is useful for high-resolution desktop NMR, MRI and mobile NMR device.

Large enhancement of superconducting transition temperature of SrBi3 induced by Na substitution for Sr.

The Matthias rule, which is an empirical correlation between the superconducting transition temperature (Tc) and the average number of valence electrons per atom (n) in alloys and intermetallic compounds, has been used in the past as a guiding principle to search for new superconductors with higher Tc. The intermetallic compound SrBi3 (AuCu3 structure) exhibits a Tc of 5.6 K. An ab-initio electronic band structure calculation for SrBi3 predicted that Tc increases on decreasing the Fermi energy, i.e., on decreasing n, because of a steep increase in the density of states. In this study, we demonstrated that high-pressure (~ 3 GPa) and low-temperature ( < 350 °C) synthesis conditions enables the substitution of Na for about 40 at.% of Sr. With a consequent decrease in n, the Tc of (Sr,Na)Bi3 increases to 9.0 K. A new high-Tc peak is observed in the oscillatory dependence of Tc on n in compounds with the AuCu3 structure. We have shown that the oscillatory dependence of Tc is in good agreement with the band structure calculation. Our experiments reaffirm the importance of controlling the number of electrons in intermetallic compounds.

Crystal structure and superconductivity of BaIr2Ge7 and Ba3Ir4Ge16 with two-dimensional Ba-Ge networks.

The Ba-Ir-Ge ternary compounds BaIr2Ge7 and Ba3Ir4Ge16 exhibit superconductivity (SC) at 2.5 and 5.2 K, respectively. Detailed single-crystal structural analysis revealed that these compounds share unique quasi-two-dimensional networks composed of crown-shaped Ge rings that accommodate Ba atoms at the center, referred to as "edge-shared crown-shaped BaGe16 polyhedra". The layered Ba-Ge network yielded a modest anisotropy of 1.3-1.4 in the upper critical field, which is in good agreement with the band structure calculations. The Ba-Ge structural unit is similar to cage structures seen in various clathrates in which the anharmonic vibration of the central atoms, the so-called "rattling" behavior, brings about strong-coupling SC. However, each Ba-Ge unit is relatively small compared to these materials, which likely excludes the possibility of unconventional SC.