Effect of Laser Power on Microstructure and Properties of WC-12Co Composite Coatings Deposited by Laser-Based Directed Energy Deposition.

During the laser-based directed energy deposition (DED-LB) processing, a WC-12Co composite coating with high hardness and strong wear resistance was successfully prepared on a 316L stainless steel substrate by adopting a high-precision coaxial powder feeding system using a spherical WC-12Co composite powder, which showed a large number of dendritic carbides and herringbone planar crystals on the substrate-binding interface. The influences of laser power on microstructural and mechanical properties (e.g., hardness, friction resistance) of WC-12Co composite surfaces were investigated. The results show that laser power has a significant effect on determining the degree of Co phase melting around the WC particles and the adhesion strength between the matrix and the coating. Lower laser power does not meet the melting requirements of WC particles, thus weakening the molding quality of the composite coating. At high laser power, it is possible to dissolve the WC particles and melt the metal powder between the particles, thus improving the material properties. The laser power increased from 700 W to 1000 W and the average hardness of the coating surface gradually increased from 1166.33 HV to 1395.70 HV, which is about 4-5 times higher than the average hardness of the substrate (about 281.76 HV). In addition, the coatings deposited at 1000 W showed better wear resistance. This work shows that the processing parameters during laser-directed energy deposition can be optimized to prepare WC-12Co composite coatings with excellent mechanical properties.

The Microstructure and Properties of Ni60/60% WC Wear-Resistant Coatings Prepared by Laser-Directed Energy Deposition.

Ni60/60% WC composite coatings with a good surface roughness and high mechanical properties were successfully prepared on 316L stainless steel substrate by laser-directed energy deposition (LDED) technology. The effects of laser power on the microstructural evolution and mechanical properties of the Ni60/60% WC composite coating were investigated. The relationships between the chemical composition, the microstructure, the hardness, and the friction wear resistance of the composite coatings were characterized and investigated. The results show that the laser power had a significant effect on the energy input, which determined the melting extent of the Ni60 phases around the WC particles and the bonding strength between the reinforcements and the matrix, as well as the bonding strength between the substrate and the coatings. With an increase in the laser power from 800 W to 1400 W, the average hardness of the coating surface increased due to the increased densification of the deposited coatings and then decreased due to grain coarsening under a high energy input. The average coefficient of friction of the coatings decreased gradually to 0.383 at 1000 W, showing a minimum wear of 0.00013 mm2 at 1200 W. The main wear mechanisms on the coated surfaces were adhesive wear and abrasive wear. Moreover, the coatings deposited at 1200 W exhibited better forming quality and wear resistance. This work suggests that the processing parameters during LDED can be optimized to prepare Ni60/60% WC wear-resistant coatings with excellent mechanical properties.