A Review on Traditional Processes and Laser Powder Bed Fusion of Aluminum Alloy Microstructures, Mechanical Properties, Costs, and Applications.

Due to its lightweight, high strength, good machinability, and low cost, aluminum alloy has been widely used in fields such as aerospace, automotive, electronics, and construction. Traditional manufacturing processes for aluminum alloys often suffer from low material utilization, complex procedures, and long manufacturing cycles. Therefore, more and more scholars are turning their attention to the laser powder bed fusion (LPBF) process for aluminum alloys, which has the advantages of high material utilization, good formability for complex structures, and short manufacturing cycles. However, the widespread promotion and application of LPBF aluminum alloys still face challenges. The excellent printable ability, favorable mechanical performance, and low manufacturing cost are the main factors affecting the applicability of the LPBF process for aluminum alloys. This paper reviews the research status of traditional aluminum alloy processing and LPBF aluminum alloy and makes a comparison from various aspects such as microstructures, mechanical properties, application scenarios, and manufacturing costs. At present, the LPBF manufacturing cost for aluminum alloys is 2-120 times higher than that of traditional manufacturing methods, with the discrepancy depending on the complexity of the part. Therefore, it is necessary to promote the further development and application of aluminum alloy 3D printing technology from three aspects: the development of aluminum matrix composite materials reinforced with nanoceramic particles, the development of micro-alloyed aluminum alloy powders specially designed for LPBF, and the development of new technologies and equipment to reduce the manufacturing cost of LPBF aluminum alloy.

Study on Mechanism of Structure Angle on Microstructure and Properties of SLM-Fabricated 316L Stainless Steel.

In this study, seven 316L stainless steel (316L SS) bulks with different angles (0°, 15°, 30°, 45°, 60°, 75°, and 90°) relative to a build substrate were built via selective laser melting (SLM). The influences of different angles on the metallography, microstructure evolution, tensile properties, and corrosion resistance of 316L SS were studied. The 0° sample showed the morphology of corrugated columnar grains, while the 90° sample exhibited equiaxed grains but with a strong <101> texture. The 60° sample had a good strength and plasticity: the tensile strength with 708 MPa, the yield strength with 588 MPa, and the elongation with 54.51%. The dislocation strengthening and grain refinement play a vital role in the mechanical properties for different anisotropy of the SLM-fabricated 316L SS. The 90° sample had greater toughness and corrosion resistance, owing to the higher volume fraction of low-angle grain boundaries and finer grains.