Fresh, Mechanical, and Durability Behavior of Fly Ash-Based Self Compacted Geopolymer Concrete: Effect of Slag Content and Various Curing Conditions.

This investigation evaluates the influence of various curing conditions and slag inclusion on the fresh, mechanical, and durability properties of self-compacting geopolymer concrete (SCGC) based on fly ash (FA). Curing temperature and curing time have a vital role in the strength and microstructure of geopolymer concrete. Therefore, to begin the research, the impacts of different curing conditions (curing temperature and curing time) and slag content on the compressive strength of FA-based SCGC were examined to determine the optimum curing method. A series of four SCGC mixes with a fixed binder content (450 kg/m3) and an alkaline/binder ratio of 0.5 was designated to conduct a parametric study. FA was replaced with slag at four different substitution percentages, including 0%, 30%, 50%, and 100% of the total weight of the binder. The fresh properties of the produced SCGC specimens were investigated in terms of slump flow diameter, T50 flow time, and L-box height ratio. Additionally, the following mechanical properties of SCGC specimens were investigated: modulus of elasticity and fracture parameters. The water permeability and freezing-thawing resistance were studied to determine the durability behavior of SCGC. In this study, the optimum curing temperature was 85 °C for the duration of 24 h, which provided the maximum compressive strength. The results confirmed that adding slag affected the workability of SCGC mixtures. However, the mechanical characteristics, fracture parameters, and durability performance of SCGC were improved for slag-rich mixtures. When using 50% slag instead of FA, the percentage increase in compressive, flexural, elastic module, and fracture energy test values were about 100%, 43%, 58%, and 55%, respectively, whilst the percentage decrease in water permeability was 65% and the resistance to freeze-thaw test in terms of surface scaling was enhanced by 79%.

Mechanical and Fracture Parameters of Ultra-High Performance Fiber Reinforcement Concrete Cured via Steam and Water: Optimization of Binder Content.

An investigational study is conducted to examine the effects of different amounts of binders and curing methods on the mechanical behavior and ductility of Ultra-High Performance Fiber Reinforced Concretes (UHPFRCs) that contain 2% of Micro Steel Fiber (MSF). The aim is to find an optimum binder content for the UHPFRC mixes. The same water-to-binder ratio (w/b) of 0.12 was used for both water curing (WC) and steam curing (SC). Based on the curing methods, two series of eight mixes of UHPFRCs containing different binder contents ranging from 850 to 1200 kg/m3 with an increment of 50 kg/m3 were produced. Mechanical properties such as compressive strength, splitting tensile strength, static elastic module, flexural tensile strength and the ductility behavior were investigated. This study revealed that the mixture of 1150 kg/m3 binder content exhibited the highest values of the experimental results such as a compressive strength greater than 190 MPa, a splitting tensile strength greater than 12.5 MPa, and a modulus of elasticity higher than 45 GPa. The results also show that all of the improvements began to slightly decrease at 1200 kg/m3 of the binder content. On the other hand, it was concluded that SC resulted in higher mechanical performance and ductility behavior than WC.