RESUMO
High-performance biosourced polylactic acid (PLA)/poly(butylene succinate) (PBS) blends with small amounts of compatibilizer, epoxy-functionalized methyl methacrylate-co-glycidyl methacrylate copolymer (PMMA-GMA), were fabricated by melt compounding. The properties of the modified PLA/PMMA-GMA, PBS/PMMA-GMA, and PLS(PLA/PBS)/PMMA-GMA blends were investigated systematically. DSC combined with X-ray diffraction revealed a low-order semi-crystalline structure for all samples. SEM and DMA showed that the compatibility between PLA and PBS was improved after addition of PMMA-GMA. Rheological behavior of blends showed that the addition of PMMA-GMA resulted in a significant improvement in the viscoelasticity. FT-IR spectra confirmed that the interfacial compatibilization between PLA and PBS phases was improved due to the reaction of epoxy groups with terminal groups of PLA and PBS. Finally, the toughness and notched impact strength of the PLA materials were increased significantly. The elongation at break and notched impact strength of PLS/PMMA-GMA was about 55.7 and 6.2 times than neat PLA after incorporation of 7 wt% PMMA-GMA, respectively.