Magnetic Graphene-Based Nanosheets with Pluronic F127-Chitosan Biopolymers Encapsulated α-Mangosteen Drugs for Breast Cancer Cells Therapy.

In this study, multifunctional chitosan-pluronic F127 with magnetic reduced graphene oxide (MRGO) nanocomposites were developed through the immobilization of chitosan and an amphiphilic polymer (pluronic F127) onto the MRGO. Physicochemical characterizations and in-vitro cytotoxicity of nanocomposites were investigated through field emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy, particle size analysis, vibrating sample magnetometer, Raman spectroscopy and resazurin-based in-vitro cytotoxicity assay. FESEM observation shows that the magnetic nanoparticles could tethered on the surface of MRGO, promoting the magnetic properties of the nanocomposites. FTIR identification analysis revealed that the chitosan/pluronic F127 were successfully immobilized on the surface of MRGO. Furthermore, α-mangosteen, as a model of natural drug compound, was successfully encapsulated onto the chitosan/pluronic F127@MRGO nanocomposites. According to in-vitro cytotoxicity assay, α-mangosteen-loaded chitosan/pluronic F127@MRGO nanocomposites could significantly reduce the proliferation of human breast cancer (MFC-7) cells. Eventually, it would be anticipated that the novel α-mangosteen-loaded chitosan/pluronic F127@MRGO nanocomposites could be promoted as a new potential material for magnetically targeting and killing cancer cells.

Facile and Green Fabrication of Microwave-Assisted Reduced Graphene Oxide/Titanium Dioxide Nanocomposites as Photocatalysts for Rhodamine 6G Degradation.

Organic pollutants, such as synthetic dyes, are treated to prevent them from contaminating natural water sources. One of the treatment methods is advanced oxidation process using a photocatalyst material as the active agent. However, many photocatalysts are hindered by their production cost and efficiency. In this study, nanocomposites consisting of reduced graphene oxide and titanium dioxide (rGO/TiO2) were prepared by a simple and green approach using the microwave-assisted method, and we utilized a graphene oxide (GO) precursor that was fabricated through the Tour method. The ratios of rGO/TiO2 in nanocomposites were varied (2:1, 1:1, and 1:2) to know the influence of rGO on the photocatalytic performance of the nanocomposites for rhodamine 6G degradation. Transmission electron microscopy (TEM) observation revealed that a transparent particle with a sheetlike morphology was detected in the rGO sample, suggesting that a very thin film of a few layers of GO or rGO was successfully formed. Based on scanning electron microscopy (SEM) observation, the rGO/TiO2 nanocomposites had a wrinkled and layered rGO structure decorated by TiO2 nanoparticles with average diameters of 125.9 ± 40.6 nm, implying that rGO layers are able to prevent TiO2 from agglomeration. The synthesized product contained only rGO and TiO2 in the anatase form without impurities that were proven by Raman spectra and X-ray diffraction (XRD). The nanocomposite with rGO/TiO2 ratio 1:2 (composite C) was found to be the best composition in this study, and it was able to degrade 82.9 ± 2.4% of the rhodamine 6G after UV irradiation for 4 h. Based on a time-resolved photoluminescence study at wavelength emission 500 nm, the average decay lifetime of R6G-rGO/TiO2 composites (2.91 ns) was found to be longer than that of the R6G-TiO2 sample (2.05 ns), implying that the presence of rGO in rGO/TiO2 composites successfully suppressed the electron-hole recombination process in TiO2 and significantly improved their photocatalytic performance. This study showed that the rGO/TiO2 nanocomposites synthesized through relatively simple and eco-friendly processes display promising prospects for photocatalytic degradation of dyes and other recalcitrant pollutants in a water stream.

The formation and antibacterial activity of Zn/ZnO nanoparticle produced in Pometia pinnata leaf extract solution using a laser ablation technique.

The single-step green synthesis has been successfully established to prepare a bi-phase structure of Zn/ZnO nanoparticles using laser ablation in a liquid medium. Nd: YAG laser with the wavelength of 1064 nm was employed to perform the laser ablation in pure water and Pometia pinnata (P. pinnata) leaf extract, with the leaf, were extracted in pure water and some concentration of ethanol. ZnO nanoparticles can be obtained via laser ablation in pure water, while the usage of P. pinnata leaf extract as the solution has caused the appearance of the bi-phase Zn/ZnO nanostructure. X-ray diffraction (XRD) pattern indicates the appearance of Zn peaks alongside with ZnO peaks with the inclusion of P. pinnata leaf extract. Transmission electron microscope (TEM) images show the change of shape from the rod-like shape into a spherical shape and smaller size spherical shape of Zn/ZnO nanoparticles in comparison with ZnO. Noticeable change of UV-visible spectrum emerges as the water was substituted by P. pinnata leaf extract. The zeta potential of Zn/ZnO prepared with P. pinnata extracted in water, with the value of - 18.9 V, reduces down to - 43.5 and - 41.1 for 20-40% of ethanol concentration, respectively. The as-prepared ZnO and Zn/ZnO colloidal samples were evaluated for their antibacterial activities against two strains Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli). Zn/ZnO sample shows a more substantial antibacterial effect in comparison with pure ZnO, no bacteria alive after 12 and 24 h' treatment for E. coli and S. aureus, respectively.

Terahertz pulse propagation in 3D-printed waveguide with metal wires component.

We report on the characterization of 3D-printed hollow core Terahertz waveguides with metal wire inclusions over a frequency range of 0.2-1.0 THz using standard THz time-domain spectroscopy. We observe single-mode broadband THz propagation in these waveguides, and measure the loss coefficient and the mode effective phase index. Our measurement data agree well with predicted values obtained from numerical simulations.