Polymer Composite Materials Based on Polylactide with a Shape Memory Effect for "Self-Fitting" Bone Implants.

The development of adaptive medical structures is one of the promising areas of bioengineering. Polymer composite materials based on polylactide (PLA) are interesting not only for their properties, such as biocompatibility, mechanical properties, biodegradation, and convenience of use, but also for demonstrating shape memory effect (SME). In this study, reducing the activation initiation temperature and the SME activation energy was achieved by forming a composite based on PLA containing 10% poly (ε-caprolactone) (PCL). The effect of the plasticizer on the structure, mechanical properties, and especially SME of the composite, was studied by DSC, SEM, FTIR spectroscopy, compression tests, and DMA. By varying the composition, the beginning of the SME activation was reached at 45 °C, and the apparent activation energy of the process decreased by 85 kJ/mol, ensuring safe and effective use of the material as a precursor for temporary self-fitting scaffolds for reconstructive surgery.

Mechanical properties and shape memory effect of 3D-printed PLA-based porous scaffolds.

In the present work polylactide (PLA)/15wt% hydroxyapatite (HA) porous scaffolds with pre-modeled structure were obtained by 3D-printing by fused filament fabrication. Composite filament was obtained by extrusion. Mechanical properties, structural characteristics and shape memory effect (SME) were studied. Direct heating was used for activation of SME. The average pore size and porosity of the scaffolds were 700µm and 30vol%, respectively. Dispersed particles of HA acted as nucleation centers during the ordering of PLA molecular chains and formed an additional rigid fixed phase that reduced molecular mobility, which led to a shift of the onset of recovery stress growth from 53 to 57°C. A more rapid development of stresses was observed for PLA/HA composites with the maximum recovery stress of 3.0MPa at 70°C. Ceramic particles inhibited the growth of cracks during compression-heating-compression cycles when porous PLA/HA 3D-scaffolds recovered their initial shape. Shape recovery at the last cycle was about 96%. SME during heating may have resulted in "self-healing" of scaffold by narrowing the cracks. PLA/HA 3D-scaffolds were found to withstand up to three compression-heating-compression cycles without delamination. It was shown that PLA/15%HA porous scaffolds obtained by 3D-printing with shape recovery of 98% may be used as self-fitting implant for small bone defect replacement owing to SME.