RESUMO
The objective of this work is to evaluate the applicability of exchange coupling between nanoparticles of Nd2Fe14B (hard magnetic material) and Fe90Al10 (soft magnetic material), as permanent magnets produced by surfactant-assisted mechanical alloying. The obtained powders were then mixed with 85% of the Nd2Fe14B system and 15% of the Fe90Al10 system and subsequently sintered at 300 °C, 400 °C and 500 °C for one hour. The results obtained by Mössbauer spectrometry (MS) show a ferromagnetic behavior with six magnetic sites represented by sextets (16k1, 16k2, 8j1, 8j2, 4c and 4e), characteristic of the Nd2Fe14B system. X-ray diffraction (XRD) results show a tetragonal and BCC structure for the Nd2Fe14B and FeAl systems, respectively. The results obtained by vibrating sample magnetometry (VSM), for mixtures of the Nd2Fe14B and Fe90Al10 sy stems sintered at 300 °C, 400 °C and 500 °C, allow for the conclusion that the coercive field (Hc) decreases drastically with temperature and the percentage of soft phase at values of Hc = 132 Oe compared to the coercive field values reported for Nd2Fe14B Hc = 6883 Oe, respectively. Images obtained by transmission electron microscopy (TEM), for the Fe90Al10 system, show a tendency for the nanoparticles to agglomerate.
RESUMO
In this work, the mechanochemical synthesis method was used for the first time to produce powders of the nanocrystalline Nd1.1Fe10CoTi compound from Nd2O3, Fe2O3, Co and TiO2. High-energy-milled powders were heat treated at 1000 °C for 10 min to obtain the ThMn12-type structure. Volume fraction of the 1:12 phase was found to be as high as 95.7% with 4.3% of a bcc phase also present. The nitrogenation process of the sample was carried out at 350 °C during 3, 6, 9 and 12 h using a static pressure of 80 kPa of N2. The magnetic properties Mr, µ0Hc, and (BH)max were enhanced after nitrogenation, despite finding some residual nitrogen-free 1:12 phase. The magnetic values of a nitrogenated sample after 3 h were Mr = 75 Am2 kg-1, µ0Hc = 0.500 T and (BH)max = 58 kJ·m-3. Samples were aligned under an applied field of 2 T after washing and were measured in a direction parallel to the applied field. The best value of (BH)max ~ 114 kJ·m-3 was obtained for 3 h and the highest µ0Hc = 0.518 T for 6 h nitrogenation. SEM characterization revealed that the particles have a mean particle size around 360 nm and a rounded shape.
RESUMO
We describe an HPRT deficiency in a 2-month-old child who presented acute renal failure and gout with normal mental and motor development for age. The patient was diagnosed with Lesch-Nyhan disease and showed a new mutation, a deletion of two bases in exon 3 of the HPRT gene (c.269-270delAT).