Partial characterization of chayotextle starch-based films added with ascorbic acid encapsulated in resistant starch.

Chayotextle starch was modified by subjecting it to a dual treatment with acid and heating-cooling cycles. This caused a decrease in the content of amylose, which showed values of 30.22%, 4.80%, 3.27% and 3.57% for native chayotextle starch (NCS), starch modified by acid hydrolysis (CMS), and CMS with one (CMS1AC) and three autoclave cycles (CMS3AC), respectively. The percentage of crystallinity showed an increase of 36.9%-62% for NCS and CMS3AC. The highest content of resistant starch (RS) was observed in CMS3AC (37.05%). The microcapsules were made with CMS3AC due to its higher RS content; the total content of ascorbic acid of the microcapsules was 82.3%. The addition of different concentrations of CMS3AC microcapsules (0%, 2.5%, 6.255% and 12.5%) to chayotextle starch-based films (CSF) increased their tensile strength and elastic modulus. The content of ascorbic acid and RS in CSF was ranged from 0% to 59.4% and from 4.84% to 37.05% in the control film and in the film mixed with CMS3AC microcapsules, respectively. Water vapor permeability (WVP) values decreased with increasing concentrations of microcapsules in the films. Microscopy observations showed that higher concentrations of microcapsules caused agglomerations due their poor distribution in the matrix of the films.

Effect of ripening and heat processing on the physicochemical and rheological properties of pepper pectins.

Water-, chelator-, and alkali-soluble pectins were isolated from raw and heat-processed Jalapeño peppers (green and red) and their physiochemical and rheological properties were determined. The yield, tristimulus color, degree of methyl esterification, monosaccharide composition, molecular weights distribution, and protein content depended on ripening and heat processing. The viscosity properties of pectins were independent of ripening. The water-soluble pectin was the most abundant pectin. Pectins from grilled peppers showed the lowest L* values. The alkali-soluble pectin showed the highest protein content. The content of xylose, rhamnose, and mannose in pectins was highly altered by tested factors. The degree of methyl esterification of pectins ranged from 26.8 to 91.6%. The peak Mw of the main fraction of tested pectins was sequentially reduced by ripening and heat processing. Pectins from raw peppers showed the best viscosity properties.

Physicochemical, antimicrobial and antioxidant properties of chitosan films incorporated with carvacrol.

Chitosan films (CF) with carvacrol (CAR) [0.5%, 1.0% and 1.5% v/v] were prepared by the emulsion method. The retained CAR, water solubility, water vapor permeability (WVP), optical, mechanical properties, antibacterial and antioxidant capacity of films were analyzed. The results indicate that the retention of CAR in the CF was ≈50%. The incorporation of CAR to CF decreased the water solubility, the WVP, the yellowing and transparency and the tensile strength, but increased the stiffness. Microcapsules with diameters of 2 to 7 µm were found on the surface CF-CAR. The CF-CAR with highest CAR concentrations showed antibacterial activity against S. typhimurium and E. coli O157:H7. The CF-CAR had higher antioxidant capacity and an increased protective effect against oxidation of erythrocytes in different grades. These results suggest potential applications of CF-CAR as active packaging to preserve food products.

Effect of ripening, heat processing, and fat type on the micellarization of pigments from jalapeño peppers.

Raw and heat-processed (boiled and grilled) jalapeño peppers at three intermediate ripening stages (brown, 50% red, and 75% red) were digested in vitro without fat and in the presence of soybean oil (SO) or beef tallow (BT), and the micellarization of their lipid soluble pigments (LSP) was measured. The micelles from digestions with brown, 50% red, and 75% red peppers contained up to 27, 35, and 29 different LSP, respectively. Boiling and grilling decreased the micellarization of LSP from brown peppers, whereas the opposite was observed with 75% red peppers. Heat processing did not clearly affect the micellarization of LSP from 50% red fruits. The impact of fat on LSP micellarization was ripening-dependent, but the micellarization of the less polar carotenoids was always increased by SO or BT. This positive effect of fat was higher with SO than with BT.

Development and characterization of edible films based on mucilage of Opuntia ficus-indica (L.).

Mucilage of Opuntia ficus-indica (OFI) was extracted and characterized by its composition and molecular weight distribution. Mucilage film-forming dispersions were prepared under different pHs (3, 4, 5.6, 7, and 8) and calcium concentration (0% and 30% of CaCl(2), with respect to mucilage's weight), and their particle size determined. Mucilage films with and without calcium (MFCa and MF, respectively) were prepared. The effect of calcium and pH on mucilage films was evaluated determining thickness, color, water vapor permeability (WVP), tensile strength (TS), and percentage of elongation (%E). The average molecular weight of the different fractions of mucilage was: 3.4 x 10(6) (0.73%), 1 x 10(5) (1.46%), 1.1 x 10(3) (45.79%), and 2.4 x 10(2) Da (52.03%). Aqueous mucilage dispersions with no calcium presented particles with an average size d(0.5) of 15.4 microm, greater than the dispersions with calcium, 13.2 microm. MFCa films showed more thickness (0.13 mm) than the MF films (0.10 mm). The addition of calcium increased the WVP of the films from 109.94 to 130.45 gmm/m(2)dkPa. Calcium and pH affected the mechanical properties of the films; the largest TS was observed on MF films, whereas the highest %E was observed on MFCa films. The highest differences among MF and MFCa films were observed at pHs 5.6 and 7 for TS and at pHs 4 and 8 for %E. No effect of pH and calcium was observed on luminosity and hue angle. Chroma values were higher for MF when compared with MFCa, and increased as pH of the films increased. Practical Application: In this study mucilage from nopal was extracted and characterized by its ability to form edible films under different pHs, and with or without the addition of calcium. Opuntia ficus-indica mucilage had the ability to form edible films. In general, it can be considered that mucilage films without modification of pH and without the addition of calcium have the best water vapor barrier properties and tensile strength. Mucilage from nopal could represent a good option for the development of edible films in countries where nopal is highly produced at low cost, constituting a processing alternative for nopal.